It is well established that halogenated fullerene derivatives act as synthetic intermediates for further substitution viareplacement with nucleophlies. In the present work, systematic studies were carried out on the synthesis of bromofullerenesunder different experimental conditions. The effect of reaction time on the product formed was observed. We observed theformation of new compound of bromofullerenes in a different stoichiometric ratio i.e., C60Br14; in addition to previousreported bromofullerenes in the stoichiometric ratio of C60Br6, C60Br8, and C60Br24. The new derivative of bromofullerene wasisolated and well characterized by various analytical techniques like FT-IR, TGA, DSC, and elemental analysis. In this paper,detail of the synthesis and characterization of the bromofullerene prepared are described. The yields obtained were better thanthose reported previously.

Granular Activated Carbon (GAC) has been proven to be an excellent material for many industrial applications. A systematic study has been carried out of the kinetics of physical as well as chemical activation of phenolic resin chars. Physical activation was carried out using CO2 and chemical activation using KOH as activating agent. There are number of factors which influence the rate of activation. The activation temperature and residence time at HTT varied in the range 550~1000℃ and ½~8 hrs respectively. Kinetic studies show that the rate of chemical activation is 10 times faster than physical activation even at much lower temperature. Above study show that the chemical activation process is suitable to prepare granular activated carbon with very high surface area i.e. 2895 m2/g in short duration of time i.e. 1 to 2 hrs at lower temperature i.e. 750℃ from phenolic resins.