Polyacrylonitrile (PAN) copolymers of different molecular weights were synthesized by a suspension polymerization and precipitation polymerization method. The rheology behaviors of the synthesized PAN copolymers were investigated in relation to their molecular weight, solid content and melting temperature. The influence of "historical effects" on the spinning solution of PAN was studied by analyzing the laws of viscosity considering the diversification time and temperature. The viscosity disciplines of each spinning solution conformed well to the rheological universal laws in a comparison of the suspension polymerization product with that of precipitation polymerization. Viscosity changes in the swelling process of dissolution were gentler in the suspension polymerization product; a small amount of water will quickly debase the solution viscosity, and high-speed mixing can greatly shorten the time required by the spinning solution to reach the final viscosity.

According to kinetic mechanisms, liquid phase polymerization and solid phase polymerization are different in acrylonitrile (AN) polymerization, and so the relationship between the contribution ratio and molecular weight distribution (MWD) was obtained through theoretic analysis. The precipitation homopolymerization of AN was carried out in a mixture solution of dimethyl sulfoxide (DMSO) and water at 50~65℃ using α,α'-azobisisobutyronitrile as an initiator. The contribution ratio decreased and approached 0; the MWD also decreased and approached 2 with the increase of the H2O/DMSO ratio from 10/90 to 90/10. The experimental data were found to coincide well with the theoretical equation derived from the mechanisms.