본 연구에서는 알킬체인의 길이가 서로 다른 benzyltrialkylammonium chloride계 화합물을 합성하여 리포좀 제조에 응용하였다. 제조된 리포좀의 평균 입도분포, 제타전위, 방출거동 및 항균성을 조사하였으며, 사슬 길이에 따른 특성을 비교하였다.리포좀의 평균 입도는 120~140 nm의 크기분포를 가졌으며 소수성 사슬의 길이가 증가할수록 큰 입 자크기를 가졌다. 리포좀 용액의 제타전위는 양이온성 계면활성제인 benzyltrialkylammonium chloride를 첨가함에 따라 +80~90 mV의 값을 가지며 향상된 분산 안정성을 보였다. 방출거동에서는 사슬 길이에 따라 방출 속도를 조절할 수 있었으며 긴 사슬의 계면활성제를 첨가한 리포좀은 증가된 서방형 방출특 성을 보였다. 또한, 리포좀의 포집효율은 25.9~27.5% 이었다.

Nowadays, the study of CFRP reinforced with carbon fiber is focused on improving the the mechanical property. The study on the fracture data of CFRP are not properly made out than that of the general mechanical joint. In this study, the fracture property of mode 1 at the same condition of tensile experiment is investigated by applying the layer angle to laminated CFRP with the thickness of 15 mm. When the reaction forces until dropping out the bonded surface are compared with the cases of the layer angles of 0°, 45° and 60°, the reaction force is shown to be most and the elapsed time until dropping out the bonded surface is longest at that of 45°. The deformation energy is also shown to have the highest value by dropping out the adhesive interface. As the basis of the analysis result of this study, the most safety with fracture resistance is shown in the case of 45°. the bonded structure applying the appropriate layer angle is thought to have the structural safety.

In this study, we study the behavior of CFT subjected to pure bending moment considering the interface character between the materials. We assume that the interface between the materials has 2 cases, one is full-composite the other is non-composite. Through the analysis of the FEM results, we find that CFT’s flexure behavior is unique compared to other composite structures. There is almost similar CFT’s flexure behavior in the pure moment regardless of interface character between steel and concrete. This is because there is no difference in the neutral axis of the full-composite and non-composite in the CFT scetion.

The synthesis of octenyl succinyl β-gucan (OSA-β-glucan) was carried out and its interfacial properties at the oil-water interface and in emulsion systems were investigated. An aqueous ethanol system as a reaction media was used to facilitate the synthesis process; 10% (w/w) ethanol found to be the best as it showed a maximum degree of substitution (DS: 0.0132). FT-IR showed a characteristic absorption spectrum at 1736cm-1, indicating the esterification of octenyl succinyl groups to β-glucan backbone. As for interfacial tension measurements, it was decreased with increasing concentration of OSA-β-glucan in the aqueous phase and when NaCl was added to aqueous OSA-β-glucan solution in the range of 0.01 M to 0.1 M and also when pH was raised (pH 3 ~ pH 9). In systems of emulsion stabilized with OSA-β-glucan, fat globule size found to decrease with increasing concentration of OSA-β-glucan, showing a critical value of about 0.32μm at 0.5 wt%. When the OSA-β-glucan emulsions were stored, it was found that fat globule size was increased with storage time and particularly pronounced increase was observed in emulsion with 1% OSA-β-glucan, possibly due to depletion flocculation. Results of creaming stability evaluated by light scattering technique showed that it was more stable in emulsions containing smaller fat globule size. Surface load of OSA-β-glucan in emulsions increased with increasing concentration of OSA-β-glucan, suggesting a multilayer adsorption.

Britsh StandardBS 7991)에 명시된 DCB 시험편을 본 연구에 맞게 수정 후 두께 25mm, 35mm, 45mm, 55mm, 그리고 65mm의 DCB시험편을 제작하였다. 이 후 시험편을 Single-lap 방식으로 접착한 후 정적실험에서 도출된 최대 전단력을 각 시험편에 10Hz로 피로하중을 가하였다. 실험 결과값에 대한 수치해석적 검증을 하고자 상용 해석 프로그램인 ANSYS를 통해 실험과 동일한 시험편과 조건 하에 해석을 수행하였다. 접착력 해석을 하기 위해서 Mesh의 절점(node)들의 관계가 매우 중요하기 때문에 접착된 부분의 모든 절점들은 동일 선상에 있게 Mesh를 형성하였다. 실험 결과와 해석 결과를 비교해 본 결과 피로하중이 약 200cycle 반복되었을 때 최대 등가응력이 발생 하였고, 이때 전단방향으로 변위가 약 11mm 진전 된 것을 볼 수 있었다. 이후 4000cycle가량 피로하중이 반복 될 동안 변위는 일정하게 점점 증가한 후 피로하중이 약 4800cycle 반복 되었을 때 실험과 해석 데이터 모두 접착계면에서 완전한 전단 파괴가 일어난 것을 볼 수 있었다. 이때 변위는 약 20mm 진행 되었다. 해석을 통해 실험 데이터를 검증해 본 결과 두 결과 값은 완전 하게 같지는 않지만 유한요소법 해석 결과에 대한 신뢰를 확보 할 수 있었다. 이는 실제 구조물에 실험 없이 간단한 재료 물성치만으로도 해석을 통하여 구조적 안전성을 알아 볼 수 있는 한 방법이 될 수 있을 것이라고 사료된다.

N,N,N-Trimethyl-10-nitrophenoxy decylammonium bromide (N10TAB) and N,N,N,N-Tetramethyl-bis-〔10-nitrophenoxy decyl〕-1,6-hexanediammonium dibromide (N10-6-10N), bearing aromatic nitrophenoxy group in the end of their hydrophobic chains have been prepared, and their properties in aqueous solutions have been studied by conductivity and H-NMR spectroscopy. Below the critical micelle concentration N10-6-10N form premicelle with two or three surfactant molecules. Beyond the critical micelle concentration two molecules have strong self-aggregation ability and form micelles of rather small size and with small aggregation numbers. H-NMR at different concentrations give the informations on the environmental changes of the surfactants on their micellization progress.

피부 노화를 방지하고 지속적으로 보습을 유지하기 위해 다양한 베시클들이 연구되고 있다. 최근에 활성물질의 흡수, 투과 및 보습의 유지와 관련하여 리포좀, 액정 및 다중층 라멜라 에멀젼 같은 많은 제조 방법들이 소개되고 있다. 본 연구에서는 인지질과 유사한 cetearyl alcohol/ceteth-20 phosphate/dicetyl phosphate 계면활성제를 이용하여 전단세기 및 pH 변화에 따른 다중층 라멜라 베시클을 개발하였으며 편광현미경을 통해 확인하였다. 결과로서 낮은 전단세기 및 pH에서는 라멜라 베시클 입자의 형태가 불균일하게 형성됨을 확인하였다. 42℃에서 2개월 간의 라멜라 베시클 내의 레티놀 함량의 변화를 측정한 결과 낮은 pH에서 레티놀의 함량이 감소하였다. 또한, 이 라멜라 베시클은 일반 O/W 에멀젼에 비해 피부 수분손실량이 14% 감소됨을 확인하였으며, O/W 썬 크림과 내수성 in vitro SPF를 측정하여 비교한 결과 UVB와 UVA 영역 모두에서 자외선을 잘 차단하여 유사한 내수성을 보이고 있음을 확인하였다.

전도성 고분자 PFO(Polyfluorene)에 양전극 ITO와 음전극으로 AI 를 추가한 단순한 양극성 구조의 ITO/PFO/Al 소자를 제작하였다. PFO에 BaTIO₃나노세라믹스 분말을 중량비로 0wt%, 10wt%, 20wt% 와 30wt% 로 달리한 4종류의 시편에 만들고, Keithley 사의 2400 Sourcemeter를 이용하여 0V에서 21V까지 DC전압을 인가하면서 소자에 흐르는 전류량을 관찰하였다. 수 나노 크기의 BaTIO₃분말의 첨가는 PFO/AI 계면에서의 전위장벽을 감소시켜 Fowler-Nordheim Tunneling이 시작되는 전압이 BaTIO₃가 첨가되지 않은 시편의 경우에 비하여 7V에서 최대 10V가 낮아진 결과를 얻었다. 소자에 흐르는 최대 전류값은 인가 전압 DC21V일 때 BaTIO₃첨가량에 비례하여 4배에서 5.5배까지 증가하였다. BaTIO₃의 첨가효과는 20wt% 이상 첨가된 경우 효과가 포화되기 시작하여, 30wt%의 BaTIO₃를 첨가한 시편의 전류량은 오히려 감소하였고 전류주입도 어려워지는 상반된 결과를 얻었다. 이것은 첨가한 나노 분말의 표면전하가 만드는 미세전계의 영향이 인접한 거리에서 서로 중첩되어 전류의 흐름이 오히려 감소하는 결과를 보인 것을 판단된다. 이로서 강유전체가 첨가된 전도성 고분자/금속 계면의 I-V 특성은 나노 세라믹스 분말의 표면전하가 만드는 국소미세전계의 영향을 받아 Trap Charge Limited Current 모델에 부합하는 결과를 가짐을 알 수 있었다.

For heat exchanger applications, 2-ply clad materials were fabricated by rolling of aluminum (Al) and mild steel sheets. Effects of annealing temperature on interface properties, especially on inter-layer formation and softening of strain hardened mild-steel, for Al/mild steel clad materials, were investigated. To obtain optimum annealing conditions for the Al/mild steel clad materials, annealing temperature was varied from room temperature to 600˚C. At the annealing temperature about 450˚C, an inter-layer was formed in an island-shape at the interface of the Al/mild steel clad materials; this island expanded along the interface at higher temperature. By analyzing the X-ray diffraction (XRD) peaks and the energy dispersive X-ray spectroscopy (EDX) results, it was determined that the exact chemical stoichiometry for the inter-layer was that of Fe2Al5. In some samples, an X-layer was formed between the Al and the inter-layer of Fe2Al5 at high annealing temperature of around 550˚C. The existence of an X-layer enhanced the growth of the inter-layer, which resulted in the delamination of the Al/mild-steel clad materials. Hardness tests were also performed to examine the influence of the annealing temperature on the cold deformability, which is a very important property for the deep drawing process of clad materials. The hardness value of mild steel gradually decreased with increasing annealing temperature. Especially, the value of hardness sharply decreased in the temperature range between 525˚C and 550˚C. From these results, we can conclude that the optimum annealing temperature is around 550˚C under condition of there being no X-layer creation.

In this study, we inserted a Zn buffer layer into a AZO/p-type a-si:H layer interface in order to lower the contact resistance of the interface. For the Zn layer, the deposition was conducted at 5 nm, 7 nm and 10 nm using the rf-magnetron sputtering method. The results were compared to that of the AZO film to discuss the possibility of the Zn layer being used as a transparent conductive oxide thin film for application in the silicon heterojunction solar cell. We used the rf-magnetron sputtering method to fabricate Al 2 wt.% of Al-doped ZnO (AZO) film as a transparent conductive oxide (TCO). We analyzed the electro-optical properties of the ZnO as well as the interface properties of the AZO/p-type a-Si:H layer. After inserting a buffer layer into the AZO/p-type a-Si:H layers to enhance the interface properties, we measured the contact resistance of the layers using a CTLM (circular transmission line model) pattern, the depth profile of the layers using AES (auger electron spectroscopy), and the changes in the properties of the AZO thin film through heat treatment. We investigated the effects of the interface properties of the AZO/p-type a-Si:H layer on the characteristics of silicon heterojunction solar cells and the way to improve the interface properties. When depositing AZO thin film on a-Si layer, oxygen atoms are diffused from the AZO thin film towards the a-Si layer. Thus, the characteristics of the solar cells deteriorate due to the created oxide film. While a diffusion of Zn occurs toward the a-Si in the case of AZO used as TCO, the diffusion of In occurs toward a-Si in the case of ITO used as TCO.

Cationic gemini-surfactant, namely 1,4-butane-bis(N-alkanoyloxyethyl-N,Ndimethyl)-diammonium bromide was synthesized and their inhibition effect on corrosion of mild steel in 1 M HCl solution was tested by weight loss method. The synthesized product was confirmed by FT-IR and 1H-NMR spectroscopy. Surface tensions were measured by surface tensiometer Sigma 70. Their c.m.c. values evaluated by surface tension method was 4.1×10-5~5.4×10-5 mol/L. The Krafft point of the these surfactants were 〈0~10.7℃. The emulsifying properties of synthesized cationic gemini surfactants and sodium dodecyl sulfate (SDS), tetradecyl trimethyl ammonium bromide (TTAB) was investigated. Of these, 1,4-butane-bis(N-lauroyloxyethyl-N,N-dimethyl)- diammonium bromide, CGL 14-4-14 has been confirmed as a good emulsifier. The inhibition efficiency increases by increasing cationic gemini surfactant concentration. As a result, these surfactants are expected to be applied as corrosion inhibitors.

Silicon heterojunction solar cells have been studied by many research groups. In this work, silicon heterojunction solar cells having a simple structure of Ag/ZnO:Al/n type a-Si:H/p type c-Si/Al were fabricated. Samples were fabricated to investigate the effect of transparent conductive oxide growth conditions on the interface between ZnO:Al layer and a-Si:H layer. One sample was deposited by ZnO:Al at low working pressure. The other sample was deposited by ZnO:Al at alternating high working pressure and low working pressure. Electrical properties and chemical properties were investigated by light I-V characteristics and AES method, respectively. The light I-V characteristics showed better efficiency on sample deposited by ZnO:Al by alternating high working pressure and low working pressure. Atomic concentrations and relative oxidation states of Si, O, and Zn were analyzed by AES method. For poor efficiency samples, Si was diffused into ZnO:Al layer and O was diffused at the interface of ZnO:Al and Si. Differentiated O KLL spectra, Zn LMM spectra, and Si KLL spectra were used for interface reaction and oxidation state. According to AES spectra, sample deposited by high working pressure was effective at reducing the interface reaction and the Si diffusion. Consequently, the efficiency was improved by suppressing the SiOx formation at the interface.

The blending effects of surfactants on the polystyrene emulsion polymerization were studied. The blending of Triton X-100 and SDS affects to the interfacial properties of the styrene monomer and water phases, and finally, the properties of the polystyrene latex particles. As the blending ratio of SDS/Triton X-100 increases, the interfacial tension and CMC of the blended surfactants were decreased and results in a reducing the size of the latex particles. It was found that the interfacial tension was reduced when the surfactant were blended. By increasing the SDS content, the interfacial tension was reduced, and, at a certain condition, the interfacial tension was reached to an extremely low value to form micro-emulsion and the nano-sized latex particles (80~110 nm).

We studied the influence of different types of metal electrodes on the performance of solution-processed zinc tin oxide (ZTO) thin-film transistors. The ZTO thin-film was obtained by spin-coating the sol-gel solution made from zinc acetate and tin acetate dissolved in 2-methoxyethanol. Various metals, Al, Au, Ag and Cu, were used to make contacts with the solution-deposited ZTO layers by selective deposition through a metal shadow mask. Contact resistance between the metal electrode and the semiconductor was obtained by a transmission line method (TLM). The device based on an Al electrode exhibited superior performance as compared to those based on other metals. Kelvin probe force microscopy (KPFM) allowed us to measure the work function of the oxide semiconductor to understand the variation of the device performance as a function of the types metal electrode. The solution-processed ZTO contained nanopores that resulted from the burnout of the organic species during the annealing. This different surface structure associated with the solution-processed ZTO gave a rise to a different work function value as compared to the vacuum-deposited counterpart. More oxygen could be adsorbed on the nanoporous solution-processed ZTO with large accessible surface areas, which increased its work function. This observation explained why the solution-processed ZTO makes an ohmic contact with the Al electrode.

2006년 10월 22일에서 24일에 걸쳐 한반도 강릉지역에서 강한 집중호우가 발생했다. 이 기간에 대해서 집중호우가 발생하기 전과 강우강도가 가장 강했을 때 나타나는 종관적, 운동학적 특성을 조사하기 위하여 본 연구에서는 지상일기도, 상층일기도, 적외위성영상, 자동기상관측장비(AWS) 자료, NCEP(National Centers for Environmental Prediction) 전구분석자료를 이용하였다. 분석 기간 동안 강릉에서 관측된 총 강수량은 316.5 mm이고, 최대 순간풍속은 63.7m s-1이다. 일기도를 분석해보면 집중호우가 시작하기 전 온대저기압이 한반도 중부에서 발달하였으며 한반도 북부에 역전기압골이 형성되어 있다. 또한 300 hPa 상층일기도에서는 서해와 한반도 남부에 제트기류가 위치하며, 위치 소용돌이도 이상과 관련된 절리 저기압이 한반도 북서부에서 발달하고 있다. 강우강도가 가장 강했을 때의 특성을 좀 더 자세히 알아보기 위하여 강릉지역의 위치 소용돌이도 이상과 바람, 위치 소용돌이도의 시간-연직 단면도, 연직운동, 발산장과 수렴장, 역학적 온위의 연직분포에 대해 조사하였다. 종관적, 운동학적 과정을 분석해 본 결과 대류권계면 접힘이 집중호우 발생에 큰 역할을 한 것으로 사료된다.

Diamond/SiC composites are appropriate candidate materials for heat conduction as well as high temperature abrasive materials because they do not form liquid phase at high temperature. Diamond/SiC composite consists of diamond particles embedded in a SiC binding matrix. SiC is a hard material with strong covalent bonds having similar structure and thermal expansion with diamond. Interfacial reaction plays an important role in diamond/SiC composites. Diamond/SiC composites were fabricated by high temperature and high pressure (HPHT) sintering with different diamond content, single diamond particle size and bi-modal diamond particle size, and also the effects of composition of diamond and silicon on microstructure, mechanical properties and thermal properties of diamond/SiC composite were investigated. The critical factors influencing the dynamics of reaction between diamond and silicon, such as graphitization process and phase composition, were characterized. Key factor to enhance mechanical and thermal properties of diamond/SiC composites is to keep strong interfacial bonding at diamond/SiC composites and homogeneous dispersion of diamond particles in SiC matrix.

The micro-structural changes, strength characteristics, and micro-fractural behaviors at the joint interface between a Sn-4.0wt%Ag-0.5wt%Cu solder ball and UBM treated by isothermal aging are reported. From the reflow process for the joint interface, a small amount of intermetallic compound was formed. With an increase in the isothermal aging time, the type and amount of the intermetallic compound changed. The interface without an isothermal treatment showed a ductile fracture. However, with an increase in the aging time, a brittle fracture occurred on the interface due mainly to the increase in the size of the intermetallic compounds and voids. As a result, a drastic degradation in the shear strength was observed. From a microshear test by a scanning electron microscope, the generation of micro-cracks was initiated from the voids at the joint interface. They propagated along the same interface, resulting in coalescence with neighboring cracks into larger cracks. With an increase in the aging time, the generation of the micro-structural cracks was enhanced and the degree of propagation also accelerated.

The rheological properties and surface tensions of polymer solutions and polymer-surfactant mixed solutions were investigated. The polymers used in this study were a homopolymer of acrylic acid crosslinked with an allyl ether of pentaerythritol, an allyl ether of sucrose, or an allyl ether of propylene (CARBOMER), acylate/C10-30 alkyl acylate crosspolymer (AAAC), and ammonium acryloydimethyltaurate/VP copolymer (ADTV). A solubilizing agent PEG-40 hydrogenated castor oil (HCO-40) and an emulsifying agent polyoxyethylene (20) sorbitan monostearate (POLYSORBATE 60) made the micelles intervening between AAAC polymers, resulting in the increase of viscosity. However, HCO-40 made this behavior over the wider range of surfactant concentration than POLYSORBATE 60. From the view point of surface tensions in the same range of surfactant concentration, AAAC/HCO-40 solution showed the area of increasing surface tension with surfactant concentration in contrast to the AAAC/POLYSORBATE 60 solution showing no increasing area.