This paper investigates tensile characteristics of the stress aging heat-treated SM45C steel which are aging temperature at 250℃, 300℃, aging time at 1, 3 hours, and applied load at 300, 400N conditions by using acoustic emission. Most suitable aging condition was aging temperature 300℃, aging time 1 hour, and aging applied load 300N. And increased yield load 28.3% than non-treatment specimen in this condition. AE energy in elastic limit increased about 16.7 times than non-treatment specimen. When aging time is 3 hours, yield load decreased than other conditions that possibility is high to have itself defect on inside the specimen or coarse grain size precipitation is different in happened over-aging phenomenon. Especially, in case of 300℃, 3 hours and 400N condition appeared AE energy in elastic limit fairly high about 30 times than non-treatment specimen. This is considered by emit a lot of energies when material causes plastic deformation because the ductility increases on specimen by over-aging phenomenon.
7050 Al합금의 응력부식저항성에 미치는 2단 시효처리의 영향을 미세조직관찰, 전기전도도시험 및 SCF값을 평가함으로써 조사하였다. 최대 경도 이상 과시효에 의해 주 강화상인 η'상이 η상으로 변태되었고, 입내 및 입계에 존재하는 η상의 크기와 간격이 커졌으며 그 결과 응력부식저항성이 증대되었다. 2차 시효시간의 증가에 따라 전기전도도값은 증가되었으나 항복강도의 감소로 인하여 SCF값은 감소되었는데, 이러한 결과는 응력부식저항성의 증가를 의미한다. AMS 4107규격을 기준으로 하였을 때 7050 Al합금 단조재의 적정시효조건은 1차시효가 120˚C에서 6시간, 2차시효는 175˚C에서 12시간이었다.