        1.
        2013.10 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        CSA, a cement mineral compound that is mainly composed of 3CaO·3Al2O3·CaSO4, generates ettringite as a hydration product after a reaction with glass (lime), gypsum and water to speed up the hardening process and enhance the strength and degree of expansion. When used as a cement admixture, there is increased production of ettringite, which can improve the initial strength in the first three days and ameliorate the reduction in the initial strength caused by the use of fly ash in particular. In this study, a hydrate analysis was performed using XRD and SEM after substitution with fly ash (30%) and CSA (8%) with the goal of observing the effect of CSA on the initial strength of a cement mixture containing fly ash. The results of the analysis showed that an addition of CSA promoted the production of ettringite and improved the initial strength, resulting in the generation of hydrates, which can effectively enhance the long-term strength of these materials.
        4,000원
        2.
        2019.01 KCI 등재 서비스 종료(열람 제한)
        콘크리트에서 염소 이온과 같은 열화물질의 이동은 응력상태 및 재령의 증가에 기인한 공극구조에 따라 변화한다. 본 연구에서는 재령 28일, 91일, 그리고 365일 양생된 OPC 콘크리트의 압축 및 인장 하중조건을 고려하여 촉진탄산화 실험을 실시하였으며, 탄산화 거동을 평가하였다. KS F 2584에 의거하여 탄산화 속도계수를 도출하였는데, 하중을 고려하지 않을 경우 탄산화 속도계수는 재령 28일 대비 재령 91일은 50.0 % 수준으로, 재령 365일에서는 44.8 % 수준으로 감소하였다. 28일 재령 시, 하중의 영향으로 인해 인장재하영역에서는 103.9 ~ 108.8 % 수준으로 압축재하영역에서는 91.9 ~ 104.6 % 수준으로 변화하였다. 재령이 증가함에 따라 탄산화 속도는 크게 감소하였는데, 30 % 인장재하영역에서는 탄산화 속도계수가 1년 경과시 47.3 % 수준으로, 60 % 인장재하영역에서는 52.5 % 수준으로 감소하였으며 30 % 압축재하영역에서는 45.8 %로, 60 % 압축재하영역에서는 44.9 % 수준으로 감소하였다. 압축재하영역 30 %에서는 공극압밀로 인해 탄산화 속도계수가 감소하였으나 하중의 증가에 따라 압축재하영역 60 %에서는 미세균열의 영향으로 탄산화 속도계수가 증가하였다. 또한 인장재하영역은 압축부와는 다르게 탄산화 속도계수가 선형적으로 증가하는 경향을 나타내었다.