The high stress, low cycle fatigue test were carried out on HT80 plates with artificial part-through notch. The LBB conditions by the net section stress approach was examined in detail. Finite element methods for the state of deformation were also applied and the results were compared with the results from experiments. From the test results, it was noted that the LBB condition in fatigue test was dependent upon the maximun load change before and after the crack penetration. The LBB criterion By the net section stress approach were slightly dependent on initial crack size. It was shown that the state of deformation can be used to predict whether the component is likely to show LBB condition or they will be broken rapidly.

복합재료가 신재생 에너지 산업 관련 구조물 및 해양 구조물에서 좀 더 신뢰도 있는 주 하중 부재로 사용되기 위하여 복합재료평판의 확률론적 비선형 초기 파단 하중과 원공과 곡률이 있는 복합재료판의 확률론적 비선형 좌굴 하중이 평가되었다. 주어진 설계 추출점에서의 확정론적 유한요소해석 결과를 바탕으로 반응면기법을 이용하여 한계상태면을 확률변수로 이루어진 2차 다항식으로 근사하였다. 또한, MPFP 근처에서 좀 더 정확하게 한계상태면을 근사하기 위하여 반복적 선형보간법이 적용되었다. 파괴확률을 평가하기 위하여 근사된 한계상태면 상에서 향상된 일계이차모멘트법과 몬테카를로법이 수행되었다. 마지막으로 파단에 영향을 주는 주요한 확률변수를 파악하기 위하여 변환된 확률변수에 대한 신뢰도지수의 감도를 계산하였다.