Phosphate coating is applied to the surface of the round bar material used in the multi-stage cold forging process for the purpose of lubrication. The film characteristics are determined according to the conditions of the phosphate film treatment process. In this study, the film properties according to the phosphate treatment conditions were defined as the coefficient of repeated friction and quantitative analysis was performed. Different friction behaviors were exhibited depending on the film properties, suggesting that optimization of the phosphate film treatment conditions is possible based on this. Finally, as a practical example, friction behavior according to the film characteristics was applied to the automotive engine bolt forming process. As a final conclusion, the need for linkage analysis with phosphating conditions for optimizing the forging process was raised. In addition, it can be seen that damage to the phosphate film should be considered in the process of predicting the limiting life of the die.

본 논문에서는 국내 공항 활주로에 적합한 마찰계수 측정 및 고무 퇴적물 제거에 대한 합리적 기준 개발을 위해 관련 해외 기준 및 연구결과에 관한 문헌을 조사하였다. 그리고 2007년 8월부터 2009년 7월까지ASFT(Airport Surface Friction Tester)장비를 이용하여 인천국제공항 활주로의 마찰계수를 측정하고 항공기 집중 착륙 지점에 대한 분석을 실시하였다. 타이어 고무의 퇴적 및 제거에 따른 마찰계수의 변화를 분석하였고 이에 미치는 계절적 영향을 포장 형식별로 조사하였다. 고무 퇴적물 제거 작업을 주기적으로 수행해도 활주로 표면의 마찰계수는 장기적으로 시간에 따라 점차 감소되는 것으로 확인되었다. 여름철 마찰계수의 변화가 다른 계절에 비해 컸으며 아스팔트 포장이 콘크리트 포장보다 계절적 영향에 민감했다. 매크로한 표면조직을 갖는 아스팔트 포장의 마찰계수가 마이크로한 표면조직을 갖는 재령 초기 콘크리트 포장의 마찰계수보다 큰 것으로 나타났다. 타이어 고무의 퇴적 및 제거에 따른 마찰계수의 변화도 아스팔트 포장에서 더 큰 것으로 확인되었다.