The purpose of this research is to investigate the statistical behavior of fatigue crack propagation(FCP) in magnesium alloy AZ31. FCP tests have been performed on compact specimens of AZ31 at load ratio conditions and maximum fatigue load conditions to obtain statistical data of FCP. It was found that the variability of fatigue crack propagation rate was significantly large at initial stage of FCP and gradually became smaller as the fatigue crack propagated. The finding of the study showed that increasing the load ratio could increase the variability of fatigue crack propagation rate at initial FCP stage. The samller the load ratio, the higher the fatigue crack propagation rate at initial stage. It was also found that the load ratio is a factor affecting the fatigue crack propagation rate in magnesium alloy.