PURPOSES : This study is to evaluate the feasibility of setting the standard of cement alkali content by using ASTM C 1260(accelerated mortar bar test) METHODS : This study analyzes the ASR(alkali silica reaction) expansion of cement mortar bar based on the changes in the aggregate type(fine, coarse), cement type(ordinary, low alkali), and replacement contents of fly ash. ASR tests were conducted according to ASTM C 1260. RESULTS : In this test results, There is no big difference in the ASR expansion between ordinary cement and low alkali cement. From this test results, it was found that the variation of cement alkali content did not have a effect on ASR expansion because mortar bar was placed in a container with sufficient alkali aqueous solution at high temperature during the test process of ASTM C 1260. CONCLUSIONS : It is evidently clear that the alkali content of cement have a effect on ASR. But ASTM C 1260 is difficult to assess this effect.

본 논문에서는 ASTM C 1260을 이용하여 국내산 골재를 대상으로 알칼리-실리카 반응 판정 결과 반응성으로 판정된 골재를 대상으로 알칼리-실리카 반응 억제효과를 고찰하기 위하여 플라이애시와 질산리튬을 사용한 시멘트 경화체의 ASTM C 1260 적용성을 평가하였다. 알칼리-실리카 반응에 의한 팽창현상이 발생하는 지역에서 CaO 함량이 낮은 플라이애시를 시멘트 중량의 10, 20, 30%를 대체하는 경우 ASTM C 1260으로 알칼리-실리카 반응 억제효과를 확인할 수 있었다. 그러나 질산리튬을 사용할 경우는 ASTM C 1260은 시편을 1N NaOH 수용액에 수침하여 80℃의 온도로 길이변화를 유도하므로 시편내에 혼입된 질산리튬 성분이 외부로 용출될 수 있기 때문에 알칼리-실리카 반응 억제효과를 도출하지 못하였다. 따라서 질산리듐의 ASR 억제효과를 확인하기 위해서는 다른 시험방법을 고려해야 한다.