Mechanical alloying (MA) by high energy ball mill of Pure chromium Powders was carried out under the nitrogen gas atmosphere. Cr-N amorphous alloy powders have been produced through the solid-gas reaction subjected to MA. The atomic structure during amorphization process was observed by X-ray and neutron diffractions. An advantage of the neutron diffraction technique allows us to observe the local atomic structure surrounding a nitrogen atom. The coordination number of metal atoms around a N atom turns out to be 5.5 atoms. This implies that a nitrogen atom is located at both of centers of the tetrahedron and octahedron formed by metal atoms to stabilize an amorphous Cr-N structure. Also, we have revealed that a Cr-N amorphous alloy may produced from a mixture of pure Cr and Cr nitrides powders by solid-solid reaction during mechanical alloying.

질소가스 분위기 중에서 Cu30V70 및 Fe30Cr70 혼합분말을 기계적 합금화 (MA)처리한 결과, 두 합금계에서 비정질화가 관찰되었다. 결정질에서 비정질상으로의 구조변화 과정을 Xtjs 회절 및 중성자 회절법에 의해 관찰되었다. 결정질에서 비정질상으로의 구조변화 과정을 X선 회절 및 중성자 회절법에 의해 관찰하였다. 그 결과, 이 합금계에서의 비정질화는 각 결정구조에서 전형적으로 존재하는 8면체 unit가 선택적으로 붕괴되어 4면체 unit로 변화되어 가는 과정임을 알 수 있었다. 또한, 중성자회절 결과로부터 질소원자는 금속원자로 이루어진 4면체의 중심에 위치하고 있음을 알 수 있었다.