According to the automated manufacturing processes followed by the development of computer manufacturing technologies, products or quality characteristics produced on the processes have measured and recorded automatically. Much amount of data daily prod

The effect of loading on chloride penetration into concrete is evaluated in this study. It is found that the chloride pene- tration rates for OPC concrete and blast furnace slag BFS concrete under the tensile stress were increased by 29% and 77%, respectively. The diffusion coefficient of FA and BFS concrete was lower than that of conventional concrete without BFS, no loads and stress states. Under tensile stress, the diffusion coefficient for FA and BFS, plain concrete showed higher values with increasing stress. The influence of specific surface area on the diffusion coefficient was investigated. As a result, the larger the specific surface areas of BFS are the lower diffusion coefficients. This tendency was more pronounced under the high stress conditions. The chloride penetration depth was distributed uni- formly when no stress was applied. However, in the case of tensile loading, the diffusion depth was not distributed uni- formly, and showed prominent characteristics. This result indicates that analysis using average values of chloride pene- tration depth is not proper under load conditions.

This study examined dynamic and characteristics and chloride penetration of concrete mixed with large amount of FA and BFS, which are considered for positive application to construction fields with purpose of long-tern durability of concrete structures. As a result of strength test on FA and BFS, FA concrete showed higher increase of strength compared to OPC, when FA4000 and FA5000 were mixed 30%, respectively. For BFS concrete, those mixed with 30% and 50% of BFS8000, respectively, showed higher or equivalent strength compare to OPC. As a result of test of chloride penetration on FA and BFS, diffusion coefficients of concrete mixed with 30% FA4000 and FA5000, respectively, showed to restrain average 6.5% of diffusion coefficient compared to OPC. And in case of BFS concrete, those mixed with BFS6000 and BFS8000, restrained diffusion of chloride ions 253% and 336%, respectively, compared to OPC. Therefore, Mixing 50% of BFS was most efficient in order to maximize restraint of chloride penetration according to metathesis of large amount. For relation between compression strength and diffusion coefficient of FA and BFS concrete, as strength increased, diffusion coefficient decreased. In this study, when mixing FA and BFS to concrete for long-run durability and restraint against chloride penetration, for FA, mixing it to concrete with less or equivalent 30% of replacement rate was most efficient. And for BFS, as fineness was higher and mixing it to concrete with less or equivalent 50% of replacement rate, there were results of higher strength compared to OPC and more efficient restraint of chloride ions.

In this study, to improve the early-age compressive strength of concrete, the powder of rapid setting additives crushed by treatment with functional grinding aid, the power-typed rapid setting cement clinker by sintering industrial waste and byproducts containing a large amount of CaO-SiO2-Al2O3 was developed. And, after adding smart BFS powder to powder of rapid setting additives, the strength tests were performed

본 연구에서는 CaO-SiO2-Al2O3가 다량 함유된 산업폐기물과 산업부산물을 소성하여 개발한 분말형 속경성 분말을 초기강도의 향상을 위해 기능성 분쇄조제로 처리하여 분쇄한 속경성 미분말을 제조하였다. 이렇게 제조된 미분말을 BFS 분말과 일정비율로 혼합한 후, 시멘트에 첨가하여 모르타르 압축강도 실험을 실시하였다. 그 결과 BFS 조기강도 향상 실험 (Series I)에서는 클링커 분쇄시 기능성 분쇄조제가 첨가되어 분쇄된 속경재가 혼합된 BFS의 초기강도 발현이 우수하며 OPC 조기강도 향상 실험 (Series II)에서는 Clinker-C에 본 실험의 기능성 분쇄조제가 첨가되어 분쇄된 속경성의 분말형 자극제가 첨가된 경우에 가장 압축강도가 높은 사실을 알 수 있었다.