The purpose of this research is to investigate the statistical behavior of fatigue crack propagation(FCP) in magnesium alloy AZ31. FCP tests have been performed on compact specimens of AZ31 at load ratio conditions and maximum fatigue load conditions to obtain statistical data of FCP. It was found that the variability of fatigue crack propagation rate was significantly large at initial stage of FCP and gradually became smaller as the fatigue crack propagated. The finding of the study showed that increasing the load ratio could increase the variability of fatigue crack propagation rate at initial FCP stage. The samller the load ratio, the higher the fatigue crack propagation rate at initial stage. It was also found that the load ratio is a factor affecting the fatigue crack propagation rate in magnesium alloy.
본 연구에서는 피로파괴에 영향을 주는 여러 인자중에서 우선 피로크랙전파에 대한 시험편 두께의 영향을 검토하기 위하여 최초 두께 25mm인 일반구조용 압연강재를 평면가공하여 두께 5, 10, 15, 20, 25mm인 CT 시험편을 가공한 후 인장-인장편진반 복피로시험을 행하여 실험한 결과 다음과 같은 결론을 얻었다. 1. 피로수명이 가장 짧게 나타나는 임의의 시험편 두께가 존재하며, 본 실험의 경우에는 두께 15m인 시험편의 경우 피로수명이 가장 짧게 나타났다. 2. 피로크랙의 발생은 두께가 두꺼운 시험편의 경우가 늦지만 피로크랙 성장은 두꺼운 시험편의 경우가 빠르게 나타났다. 3. 본 실험에서 paris시의 계수 m의 값은 절위는 1.98~4.59로서 시험편의 두께가 두꺼울수록 m의 값이 크게 된다.(이 논문의 결론부분임)