Free-radical copolymerization of glycidyl methacrylate(GMA) and N-phthalimidoethyl acrylate(NPEA) were carried out at 60℃ in dimethylformamide(DMF) solution in the presence of benzoylperoxide(BPO) at low conversion. The polymers were characterized by IR and 1H-NMR. The compositions of the copolymer was analyzed by ultra violet(UV/Vis) spectrophotometry. The reactivity ratios of the monomer was determined by the application of Fineman-Ross(FR) and Kelen-Tudos(KT) methods. The monomer reactivity ratios of the system and Alfrey-Price's resonance effect(Q) and polar effect(e) value for NIEA were determined as follow. The reactivity ratios of the monomer obtained from FR and KT are found to be r1=0.87, r2=0.98 and r1=0.88, r2=0.99 respectively. The Q and e values of poly(GMA-co-NPEM) calculated from r1 and r2 was Q= 1.31, e=0.75 respectively.

In this work, the effect of glycidyl methacrylate grafted multi-walled carbon nanotubes (GMA-MWCNTs) on the viscoelastic behaviors of polypropylene (PP) based nanocomposites was studied. The GMA-MWCNTs/PP was prepared using a bravender at 200℃ by melt mixing as a function of GMA-MWCNT content. The viscoelastic behaviors of GMA-MWCNTs/PP nanocomposites were measured by a rheometer. It was found that the GMA-MWCNTs were homogeneously dispersed in the PP matrix. The GMA-MWCNTs/PP nanocomposites showed higher storage modulus, loss modulus, and shear viscosity compared to pure PP nanocomposites and the maximum value was shown at 2.0 wt% GMA-MWCNTs loading. These results were probably attributed to the strong interfacial interaction between the GMA-MWCNT and the PP matrix.