Abstract In this study, we investigated that the activated carbon (AC)-based supercapacitor and introduced SIFSIX-3-Ni as a porous conducting additive to increase its electrochemical performances of AC/SIFSIX-3-Ni composite-based supercapacitor. The AC/SIFSIX-3-Ni composites are coated onto the aluminum substrate using the doctor blade method and conducted an ion-gel electrolyte to produce a symmetrical supercapacitor. The electrochemical properties of the AC/SIFSIX-3-Ni composite-based supercapacitor are evaluated through cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and galvanostatic charge/discharge tests (GCD). The AC/SIFSIX-3-Ni composite-based supercapacitor showed reasonable capacitive behavior in various electrochemical measurements, including CV, EIS, and GCD. The highest specific capacitance of the AC/SIFSIX-3-Ni composite-based supercapacitor was 129 F g−1 at 20 mV s−1.

Lithium ion battery are one of representative rechargeable batteries with high energy density, tiny memory effect, and low self-discharge and composed of anode, cathode, electrolyte, and membrane separator. The importance of membrane separator has been improved further as electric vehicle market increases rapidly. The conventional membrane separators are based on polyolefin (e.g., polyethylene and/or polypropylene). In case of lithium ion battery with a high capacity, polyolefin membrane separators are suffering from low thermal resistance and easy short-circuit formation leading to overheating. For these reasons, in this study, gel polymers are in-situ synthesized in electrolytes used as solvent, which are located in pores of polyolefin separators to obtain gel polymer electrolyte-polyolefin reinforced membranes.

다공성 Poly(propylene) 분리막의 지지 하에 전해질 용액 (EC/DEC 1 : 1 혼합물 내의 LiPF6 1 M 용액) 내에서 DEGDMA [Di(ethylene glycol) dimethacrylate]의 70℃ 열중합을 통하여 겔 고분자 전해질(GPE)막이 합성 되었다. 합성된 겔 고분자 전해질막의 이온전도도 및 전기화학적 안정성은 AC 임피던스법 및 CV (cyclic voltametry)법에 의하여 측정 평가하였다. 겔 고분자를 전해질로, 그리고 양극 및 음극으로는 각각 LiMi0.8Co0.2O2 및 graphite로 이용하여 리튬이온전지(LIB)도 제작하였다. 열중합을 통하여 리튬 이온전지에 적합한 이온전도도(10 -3 S/cm 이상) 및 전기화학적 안정성을 보이면서 자체적인 성상을 유지하는 겔 고분자 전해질막을 얻을 수 있었다. 단량체 함량 5%의 전구체로 제작한 겔 고분자 전지는 단량체 함량이 7.0% 및 10.0%인 경우에 비하여 우수한 고율 및 충-방전 효율을 보였다.