The anion exchange membrane fuel cells (AEMFCs) have been known to be promising eco-friendly power sources. To develop AEMFCs, the high ion conductivity, good dimensional, mechanical and alkaline stabilities are required for AEMs. However, the high conductivity generally requires high water uptake, which causes an enhanced swelling and decreased mechanical properties for the AEMs. To overcome this problem, we introduced an ionic conductor having long alkyl diammonium groups to alkyl-substituted poly(p-phenylene oxide) (PPO). Addition of this new additive increased the conductivity, mechanical and alkaline stabilities due to the molecular interaction between alkyl chains in PPO and same group of the additive. Synthesis and properties of the corresponding membranes will be discussed in detail.

수처리 공정에 대한 관심도가 매우 높음에 따라 본 연구에서는 이온교환막에 사용되는 이온교환수지를 대신할 물질로 이온그룹을 도입한 입자를 제조하였다. 기존의 이온교환 수지보다 나노 단위의 입자가 표면적으로 증가시켜 더 높은 이온교환능이 기대된다. 양이온은 –NH3 +,-NR3 +,-PR3 +,-SR2 +등의 관능기를 그리고 음이온은 -SO3 -,-COO-,-PO3 -,-C6H4O-등의 관능기를 도입한 단분산된 나노크기의 입자를 제조하여 각각 양전하와 음전하로 높게 하전시킬 수 있다. 입자들에 대해 제타전위를 측정하고, IEC, FT-SEM 및 FR-IR을 측정하여 특성평가를 진행하였다.

이온교환막은 전기투석, 연료전지 외에도 수처리 공정에 있어 관심도가 매우 높다. 본 연구에서는 이온교환막에 사용되는 이온교환수지를 대신할 물질로써 입자를 제조하였다. 나노단위의 입자가 표면적을 증가시켜 기존의 이온교환수지보다 더 높은 이온교환능이 기대된다. 단분산된 나노크기의 입자를 제조하여 양이온은 -NH3+,-NR3+,-PR3+,-SR2+등의 관능기를 그리고 음이온은 -SO3-,-COO-,-PO3-,-C6H4O-등의 관능기를 도입함으로써 각각 양전하와 음전하로 높게 하전시킬 수 있다. 입자를 제조하고 이에 따른 제타전위를 측정하고 IEC, FT-SEM, TGA 및 FT-IR을 측정하여 특성을 파악하였다.