Generally, a silicone rubber and a chlorinated polyethylene(CPE) have been used as a binder for the development of high-performance composite EM(Electro Magnetic) wave absorbers. In this paper, the EM wave absorption performance of natural lacquer, which is newly proposed as a binder was investigated. The prepared MnZn ferrite EM wave absorbers are mixed with natural lacquer showed excellent EM wave absorption characteristics compared with MnZn ferrite EM wave absorbers which are mixed with the conventional binders. MnZn ferrite EM wave absorbers mixed with natural lacquer were prepared and their absorption ability was also investigated The EM wave absorbers are fabricated in different proportions of MnZn, or NiZn ferrite and natural lacquer, and their reflection coefficients are measured. The permittivity and permeability are calculated by using the measured reflection coefficients. The EM wave absorption abilities are calculated according to different thicknesses of the EM wave absorbers.

고성능 복합형 전자파 흡수체를 개발하기 위해 종래에는 지지재로서 주로 Silicone 고무나 CPE(Chloride Polyethylene)가 사용되어 왔다. 본 연구에서는 전통 공예에서 사용되어 오던 옻에 대한 특징을 분석하고 옻의 전자파 흡수능을 실험을 통하여 평가하였다. 또한, 옻을 지지재로 사용하여 MnZn 페라이트와 배합하여 전자파 흡수체를 제작한 경우의 전자파 흡수능 및 흡수체의 두께에 따른 흡수능을 실험적으로 평가하였다. 옻을 지지재로 한 MnZn 페라이트 복합형 전자파 흡수체는 CPE나 Silicone 고무를 지지재로 한 전자파 흡수체에 비하여 우수한 전파흡수특성 나타내었으며, 옻을 지지재로 사용한 전자파흡수체의 두께 변화에 따라 정합주파수와 전파흡수능이 변화하는 것으로 나타났다.

천연세라믹, 옻칠, 그리고 고무의 전파흡수능을 조사하였다. 천연세라믹은 2.5GHz~4.5GHz의 주파수 범위에서 2.5dB이상의 전파흡수능을 나타내었으며 옻칠의 전파흡수능이 기존에 전파흡수체의 지지재로 이용되는 고무에 비해 우수한 전파흡수능을 갖고 있음을 확인하였다. 페라이트에 옻칠을 지지재로 이용한 전파흡수체에 대하여 시뮬레이션 한 결과 0.5GHz~10GHz의 주파수 범위에서 16dB 이상의 우수한 전파흡수능을 나타내었다. 따라서 기종에 지지재로 이용하던 고무대신 본 연구에서 새롭게 제안하는 옻칠을 전파흡수체의 지지재로 이용하는 것이 광대역에서 우수한 전파흡수체를 얻을 수 있을 것으로 예상된다.