The effects of different plasma agent species ( CF4, N2) over the conductivity of CFX cathode material were identified. Both plasma treatments have surface etching effect, while the CF4 plasma treatment has C–F bond modification effect and the N2 plasma treatment has defluorination effect. The changes of surface chemical species and porosity along the plasma agent were elucidated. Moreover, the electrochemical properties of plasma-treated CFX confirmed the effects of plasma treatments. The charge-transfer resistance of plasma-treated CFX was maximum 60.3% reduced than the pristine CFX. The effects of surface chemical modification coupled with etching along the plasma gas agents were compared and identified with their reaction mechanisms.

본 연구의 목적은 PET를 재활용하여 만든 물질재생 PET사를 함침공정을 통해 고전도성의 E-textile로 제작하는 것이다. 소수성의 성질을 가지고 있는 PET사는 virgin과 recycled 모두 함침공정을 통해 전자섬유로 제작되었을 때에 높은 전도성을 부여하기 힘들다는 특징이 있다. 함침공정의 효율성 향상을 위해 FEMTO SCIENCE사의 Covance-2mprfq 모델을 사용하여 재생 PET사로 이루어진 시료를 50w 5분, 10분간 플라즈마로 표면 개질하였다. 이 후 SWCNT 분산액(.1wt%, cobon 사)에 5분간 시료를 담근 후 패딩기(Padder, DAELIM lab)를 통해 시료 안쪽으로 용액이 잘 스며들도록 Dip-coating 진행하였다. 공정이 완료된 후 저항측정을 양끝점에서 멀티미터를 통해 측정하 고 좀 더 넓은 전극을 통해 정밀하게 다시 측정하였다. 고찰한 결과 플라즈마 표면 개질을 통해 함침공정을 통한 고전도성 부여가 가능해졌음을 확인할 수 있었다. 10분간 표면 개질한 경우 저항이 최대 2.880배 감소하였다. 본 연구결과를 기반으로 스마트 웨어러블 분야에서 활용되는 E-textile 또한 recycle 소재로 제작함으로써 석유자원을 절약하고 탄소배출량을 감소시킬 수 있는 스마트 웨어러블 제품을 개발하고자 한다.