A method of functionalization of multi-walled carbon nanotube (MWNT) at room temperature using dry ozone gas is described. The resulting MWNT were characterized by Fourier transform infrared, x-ray photoelectron spectroscopy, and scanning electron microscopy. Combined to these analyses and solubility in liquids, it could be concluded that the dry ozone gas exposure introduces polar functional groups such as carboxylic groups to MWNT similar to acidic modification of MWNT. Particularly, the stable dispersion of MWNT in water after ozone treatment above a critical level could be obtained, implying potential bio-application. The hydrophilic functional groups on the MWNT introduced by ozone oxidation were helpful in improving the interaction with functional groups in PA6 such as -NH2 and -CONH- resulting in improved mechanical properties.

세라믹 전구체로서 PCS와 PMS 두 종류의 실린콘 고분자를 합성하여 7, 15, 33 wt.%의 Mo분말, Mo(CO)6 금속화합물과 혼합한 뒤 1300˚C이상 가열하면 탄화물과 규화물의 다양한 세라믹복합재로 전이되었다. 특히 PMS용액에 7, 15 wt.% Mo분말을 분산하여 초음파 처리하면 열분해 수율이 60%까지 개선되고 전도성 소재인 SiC/MoSi2 복합조성의 세라믹스가 합성되었다. 그러나 풍부한 유기 반응기를 가진 PCS와 카보닐기가 탄소공급원으로 작용하는 Mo(CO)6를 반응물로 사용하였을 때는 SiC와 Mo2C와 같은 탄화물과 미향의 MoSi2 그리고 미확인상을 포함한 세라믹 복합상들이 얻어졌다.