High-entropy alloys (HEAs) are characterized by having five or more main elements and forming simple solids without forming intermetallic compounds, owing to the high entropy effect. HEAs with these characteristics are being researched as structural materials for extreme environments. Conventional refractory alloys have excellent hightemperature strength and stability; however, problems occur when they are used extensively in a high-temperature environment, leading to reduced fatigue properties due to oxidation or a limited service life. In contrast, refractory entropy alloys, which provide refractory properties to entropy alloys, can address these issues and improve the hightemperature stability of the alloy through phase control when designed based on existing refractory alloy elements. Refractory high-entropy alloys require sufficient milling time while in the process of mechanical alloying because of the brittleness of the added elements. Consequently, the high-energy milling process must be optimized because of the possibility of contamination of the alloyed powder during prolonged milling. In this study, we investigated the hightemperature oxidation behavior of refractory high-entropy alloys while optimizing the milling time.

본 연구는 압연공정에서 발생하는 폐수 중에 함유되어있는 난분해성 COD 물질을 80μm 두께의 극세사 형태로 제조된 Cu-Zn 금속합금의 산화 작용으로 인하여 발생하는 OH 라디칼을 이용하여 처리하는 방법에 관한 기초 연구이다. OH 라디칼은 유기화합물(RH) 속에 포함된 수소를 수소추출반응(H Abstraction) 또는 탄소와 탄소(C-C)의 불포화 결합에 첨가됨으로써 빠르고 비 선택적인 반응을 수행하는 것으로 알려진 것처럼 난 분해성 유기화합물의 처리에 효과적인 것으로 나타났다. 금속합금 반응 물질은 극세사 형태로 표면적이 넓어서 1회 처리만으로도 수용액의 pH를 평형에 도달하게 하여서 반응 효율성이 높은 것으로 나타났다. COD처리 효율은 중성 pH에 가까운 pH 7, pH 6에서 최고치를 보였으며 산성분위기인 pH 5이하 및 알칼리성 분위기인 pH 8이상에서는 낮은 효율을 보였다. 실제 압연 폐수의 응집 침전을 이용한 COD 처리에서도 redox 반응장치의 유무에 따라 2배 이상의 처리효율의 차이를 보였다.