In this study, two types of SKD61 tool-steel samples are built by a selective laser melting (SLM) process using the different laser scan speeds. The characteristics of two kinds of SKD61 tool-steel powders used in the SLM process are evaluated. Commercial SKD61 tool-steel power has a flowability of 16.68 sec/50 g and its Hausner ratio is calculated to be 1.25 by apparent and tapped density. Also, the fabricated SKD61 tool steel powder fabricated by a gas atomization process has a flowability of 21.3 sec/50 g and its Hausner ratio is calculated to be 1.18. Therefore, we confirmed that the two powders used in this study have excellent flowability. Samples are fabricated to measure mechanical properties. The highest densities of the SKD61 tool-steel samples, fabricated under the same conditions, are 7.734 g/cm³ (using commercial SKD61 powder) and 7.652 g/cm3 (using fabricated SKD61 powder), measured with Archimedes method. Hardness is measured by Rockwell hardness testing equipment 5 times and the highest hardnesses of the samples are 54.56 HRC (commercial powder) and 52.62 HRC (fabricated powder). Also, the measured tensile strengths are approximately 1,721 MPa (commercial SKD61 powder) and 1,552 MPa (fabricated SKD61 powder), respectively.

본 논문에서는 OFDM 방식의 문제점으로 지적되고 있는 송신단에서의 PAR 특성을 고려하여 고속 적응형 PTS 기법과 SLM 기법을 결합한 SLM-PTS 결합기법을 제안하였다. 또한, PAR 저감기법을 적용한 시스템을 평가하기 위하여 ETD-Turbo 부호를 사용한 COFDM 시스템을 구성한 후 성능을 평가하였다. 분석 결과 제안된 SLM-PTS 기법이 연산량을 경감시키며 전반적으로 우수한 PAR 저감성능을 보임을 알 수 있었다. 특히 Combine 3의 경우 10-5 BER을 기준으로 약 3.7~3.9 dB 정토의 개선된 PAR 성능을 보였다. 또한, 터보부호를 사용한 경우 전반적으로 우수한 PAR 성능을 보임을 알 수 있었고, ETD-Turbo 부호를 적응한 경우 추가적으로 약 0.5 dB 정도의 성능 개선효과가 있음을 알 수 있었다.