The phase stability of tetragonal phase in Y-TZP was investigated in terms of the distribution of grain sizes and heat-treating atmosphere. Y-TZP with various grain sizes were prepared using duration time at 1600℃ as experimental parameter. Accumulated grain size distributions were built from the SEM micrographs and the amount of tetragonal phase were measured using XRD. Both results were compared to determine the critical grain size before and after heat-treatment in vacuum. The critical grain size drastically decreased compared with the small increase of average grain size due to the autocatalytic effect which critically affects the tetragonal to monoclinic phase transformation. After heat-treatment in reductive atmosphere critical grain size relatively increased due to the stabilization of tetragonal phase. The formation of oxygen vacancies during heat-treatment was ascribed to the increase of stability.

2mol%의 이트리아로 안정화된 정방정상 지르코니아 분말을 800˚C부터 1500˚C 까지 온도별로 열처리하여 분말내 입자크기 및 입자간에 존재하는 구속력을 변화시킨 다음, 정방정상의 전이도 및 안정화효과가 무열상전이, 응력유기상전이, 등온상전이 에 미치는 영향을 고찰하였다. 그 결과 Y-TZP 분말내 정 방정상의 전이도는 고용체의 양이 일정할 경우 열처리온도의 변화에 따른 입자크기와 입자간에 존재하는 구속력의 크기에 의존하였는데 열처리온도가 증가함에 따라 전이도가 점차 증가하여 1300˚C로 열처리한 분말에서 최대값을 보였다. 그러나 1300˚C 이상으로 열처리한 분말에서는 열처리온도가 증가함에 따라 구속효과의 증가에 따라 전이도가 정차로 감소하였다. 전이도가 큰 분말에서는 정방정상이 무열상전이, 응력유기상전이, 등온상전이를 쉽게 일으켜 단사정상으로 전이하였다.