To remove SO2 from flue gas, a thin film nanocomposite (TFN) hollow fiber membrane was decorated with Nafion/TiO2 nanoparticles. Morphological and structural analyses of the TFN membranes were performed using FTIR, SEM, EDX, TEM, and AFM. The gas permeation experiments were performed with pure gases and a mixed gas within a pressure range of 1-3 bar and feed gas flow rate of 0.03-0.15 L/min. The obtained experimental results suggest that the addition of Nf/TiO2 nanoparticles improved the membrane performance by introducing sulfonate and hydroxyl functional groups to the membrane, and thus increased SO2 permeability and selectivity. The SO2 permeability was found to be 411-1671 GPU, while the ideal selectivities achieved for SO2/N2 and SO2/CO2 were 2928 and 72, respectively. Overall, an SO2 removal efficiency of 93% was achieved by using the Nf/TiO2 incorporated TFN membrane.

본 연구에서는 정제되지 않은 ZnO 및 TiO₂나노입자를 M4배지에 노출시켜 두 나노입자가 어느 정도 크기의 응집체로 변화되는지를 살펴보고 또한 두 나노입자가 수생태계 생물종인 Daphnia magna에 어떠한 영향을 초래하는지 유영저해 및 폐사율을 통해 살펴보았다. ZnO 및 TiO₂나노입자의 분말상태 크기는 각각 20 nm와 40 nm였지만, M4배지에서는 1333 nm와 1628 nm로 약 40~70배의 크기로 응집되었다. 유영저해의 경우 ZnO와 TiO₂나노입자 모두 시간 및 농도가 높아질수록 D.magna가 유영하는데 영향을 미친 것으로 나타났으며, 특히 ZnO나노입자가 TiO₂나노입자에 비해 더 큰 영향을 미치는 것으로 나타났다. 폐사율의 경우 ZnO나노입자에서는 시간 및 농도가 높아질수록 폐사되는 비율이 높았으며, TiO₂나노입자에서는 72시간이 경과된 시점의 10 ppm 이상의 농도에서 폐사하는 것으로 관찰되었다. 이는 나노입자가 해양에 유입됨으로 인해 원래의 크기에 비해 응집되어 증가되어진다는 것을 알 수 있으며, 또한 그 응집체로 인해 수생태계 생물에 영향을 주는 것으로 나타났다.