In this research, we were prepared the glazed ceramic samples by the change of the pigment content and investigated to reveal the standardized color. The chemical composition of the pigment was analyzed using a ICP-OES. XRF mapping and UV-Vis spectroscopy were used to evaluate the color property and surface homogeneity. The color development was observed as a result of analyzing the pigment content and change of the color. The pigment content and the spectral reflection showed the relation of the inverse proportion and the standardized color which could be revealed through analysis data.

Expanded graphite (EG) is synthesized by chemical intercalation of natural graphite (NG) and rapid expansion at high temperature, with titanium n-butoxide (TNB) used as titanium source by a sol-gel method to prepare EG-TiO2 composite. The performances of the prepared EG-TiO2 composite are characterized by BET surface area measurement, scanning electron microscopy (SEM), X-ray diffraction patterns (XRD) and energy dispersive X-ray analysis (EDX). To compare the photocatalytic activities of the EG-TiO2 composite, three kinds of dye solutions, methylene blue (MB), methylene orange (MO) and rhodamine B (RhB), and two kinds of light source, UV light and visible light (VL), are used. Comparing the results, it can be clearly seen that the degradation of all of the dye solutions under irradiation by UV light is much better than that under irradiation by visible light, and the decomposition of MB solution was better than that of both of MO and RhB solution.

염산매질에서 산화/환원제를 사용하여 Pu 산화수를 조절한 후, UV-Visible-Near IR 분광기를 이용하여 Pu(III, IV, V, VI) 산화수에 대한 흡수스펙트럼을 측정하여 그 분광학적 특성을 고찰하였다. Pu(III)으로 조절하기 위하여 환원제인 HCl를 사용하였으며, Pu(IV)와 Pu(VI)로 조절하기 위하여 산화제인 및 를 각각 사용하였다. 또한 Pu(VI)로 조절된 용액에 환원제인 HCl를 사용하여 Pu(V)로 조절하였다. Pu(III)와 Pu(IV)의 대표적인 흡수피크는 470 nm 및 600 nm에서 각각 관찰되었고, Pu(VI)와 Pu(V)의 특성피크는 830 nm 및 1135nm에서 각각 관찰되었다. Pu(III, IV, VI) 산화상태의 시간 경과에 따른 흡수스펙트럼 변화는 관찰되지 않았으나 Pu(V)의 경우 매우 불안정하여 생성되자 마자 Pu(III)로 변화되었다.