Bond stress between cast-in-place ductile fiber reinforced cementitious composites and CFRP plank were experimentally analyzed. As failure shape, the mixture of failure between CFRP plank and epoxy, and failure between concrete and epoxy was shown. In case of RFCON from the suggested simple bond slip relationship, the maximum average bond stress was 5.39MPa, the initial slope was 104.09MPa/mm, and the total slip length was 0.19mm. PPCON showed the maximum average bond stress of 4.31MPa, the initial slope of 126.67MPa/mm, and the total slip length of 0.26mm, while RFCON+ appeared to have 8.71MPa, 137.69MPa/mm, 0.16mm. PPCON+ had 6.19MPa maximum average bond stress, 121.56MPa/mm initial slope, and 0.34mm total slip length. To comprehend the behavior of composite structure of FRP and concrete, local bond slip relation is necessary, and thus a simple relation is suggested to be easily applied on hybrid composite system

최근에 상용 FRP 판(plank)을 콘크리트 구조물의 영구 거푸집 및 보강재로 이용하기 위한 연구가 진행되고 있다. FRP 판과 타설 콘크리트가 합성효과를 발휘하기 위해서는 두 재료간의 부착이 중요한 요인 중의 하나이다. 이러한 부착을 확보하기 위하여 FRP 판에 모래를 일반적으로 건설현장에서 많이 사용하는 에폭시를 이용하여 부착하였다. FRP 판과 콘크리트 합성구조의 구조적 거동을 이해하기 위해서는 FRP판과 타설 콘크리트 사이의 정량적인 국부 부착모델이 필요하다. 본 연구에서는 이와 같은 합성구조 시스템에 간단히 적용할 수 있는 단순 부착모델을 제안한다.