We synthesized Fe-doped TiO2/α-Fe2O3 core-shell nanowires(NWs) by means of a co-electrospinning method anddemonstrated their magnetic properties. To investigate the structural, morphological, chemical, and magnetic properties of thesamples, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and X-ray photoelectronspectroscopy were used, as was a vibrating sample magnetometer. The morphology of the nanostructures obtained aftercalcination at 500oC exhibited core/shell NWs consisting of TiO2 in the core region and α-Fe2O3 in the shell region. In addition,the XPS results confirmed the formation of Fe-doped TiO2 by the doping effect of Fe3+ ions into the TiO2 lattice, which canaffect the ferromagnetic properties in the core region. For comparison, pure α-Fe2O3 NWs were also fabricated using anelectrospinning method. With regard to the magnetic properties, the Fe-doped TiO2/α-Fe2O3 core-shell NWs exhibited improvedsaturation magnetization(Ms) of approximately ~2.96emu/g, which is approximately 6.1 times larger than that of pure α-Fe2O3NWs. The performance enhancement can be explained by three main mechanisms: the doping effect of Fe ions into the TiO2lattice, the size effect of the Fe2O3 nanoparticles, and the structural effect of the core-shell nanostructures.

Well-distributed SnO2-Sn-Ag3Sn nanoparticles embedded in carbon nanofibers were fabricated using a co-electrospinning method, which is set up with two coaxial capillaries. Their formation mechanisms were successfully demonstrated. The structural, morphological, and chemical compositional properties were investigated by field-emission scanning electron spectroscopy (FESEM), bright-field transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). In particular, to obtain well-distributed SnO2 and Sn and Ag3Sn nanoparticles in carbon nanofibers, the relative molar ratios of the Ag precursor to the Sn precursor including 7 wt% polyacrylonitrile (PAN) were controlled at 0.1, 0.2, and 0.3. The FESEM, bright-field TEM, XRD, and XPS results show that the nanoparticles consisting of SnO2-Sn-Ag3Sn phases were in the range of ~4 nm-6 nm for sample A, ~5 nm-15 nm for sample B, ~9 nm-22 nm for sample C. In particular, for sample A, the nanoparticles were uniformly grown in the carbon nanofibers. Furthermore, when the amount of the Ag precursor and the Sn precursor was increased, the inorganic nanofibers consisting of the SnO2-Sn-Ag3Sn nanoparticles were formed due to the decreased amount of the carbon nanofibers. Thus, well-distributed nanoparticles embedded in the carbon nanofibers were successfully synthesized at the optimum molar ratio (0.1) of the Ag precursor to the Sn precursor after calcination of 800˚C.