The demand for environmental consideration is on the increase in civil engineering. This study focuses on the development of technology to reduce the use of carbonate cement and improve its performance by using a silicate mineral and hardening agents, and presents the test results for the demonstrative evaluation of the properties of the raw material. Highly active feldspar was used as a binder to augment the bonding of the carbonate cement, and their change in strength was observed after test piece construction with the addition of soluble hardening agent. The uniaxial compression strength of the test piece of the general Portland cement with the addition of 0.5% soluble hardening agent, showed an increase by 33% and that of the test piece of cement with the addition of 70% substituted with feldspar increased by 28%. The strength of viscous soil; classified as soft ground, showed an increase of a maximum of 1.7 times when it was mixed with cement and solidifier depending on the curing period. These tests confirmed that a soluble solidifier is effective for improving the strength of a cement binder and that the highly active feldspar can be used as a binder.

팽창재는 콘크리트의 건조/자기수축으로 인한 균열에 매우 효과적인 혼화재료이며 콘크리트 내부 철근에 화학적 프리스트레스를 인가할수 있다. 본 논문에서는 CSA 팽창재에 의해 화학적 프리스트레스가 도입된 모르타르의 인장경화성능을 평가하였다. 철근으로 내부구속이이루어진 철근 모르타르 시편에 대하여 일축인장시험을 수행하였으며, 균열거동 특성과 인장경화 특성을 분석하였다. CSA 모르타르에서는 압축강도 및 탄성계수는 약간 감소하였으나, 화학적 압축응력이 철근에 도입되었으며, 일반 모르타르 부재에 비해 167.5% 초기균열하중이증가하였다. 높은 인장경화특성을 평가하였으며, 기존의 인장연화모델과 실험값을 비교하여 기존 제안식의 보완점을 제시하였다.