        2024.09 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        Cu-Ti thin films were fabricated using a combinatorial sputtering system to realize highly sensitive surface acoustic wave (SAW) devices. The Cu-Ti sample library was grown with various chemical compositions and electrical resistivity, providing important information for selecting the most suitable materials for SAW devices. Considering that acoustic waves generated from piezoelectric materials are significantly affected by the resistivity and density of interdigital transducer (IDT) electrodes, three types of Cu-Ti thin films with different Cu contents were fabricated. The thickness of the Cu-Ti thin films used in the SAW-IDT electrode was fixed at 150 nm. As the Cu content of the Cu-Ti films was increased from 31.2 to 71.3 at%, the resistivity decreased from 10.5 to 5.8 × 10-5 ohm-cm, and the density increased from 5.5 to 7.3 g/cm3, respectively. A SAW device composed of Cu-Ti IDT electrodes resonated at exactly 143 MHz without frequency shifts, but the full width at half maximum (FWHM) values of the resonant frequency gradually increased as the Cu content increased. This means that although the increase in Cu content in the Cu-Ti thin film helps to improve the electrical properties of the IDT electrode, the increased density of the IDT electrode deteriorates the acoustic performance of SAW devices.
        4,000원