In this study, isophorone diisocyanate (IPDI) and dimethylolbutanoic acid (DMBA) were used on the basis of poly caprolactone diol (3M, 3.5M, 4M, 4.5M) for the synthesis of water-based polyurethanes for coating on skin layers of leather. Tensile strength, elongation, and adhesive strength of the prepared samples were measured. As a result of measuring the tensile strength, the tensile strength was found to be 4.09 kgf / mm2 when 3 moles were applied, and 1.071 kgf / mm2 when 4.5 moles were applied. Elongation was 366 % when 3 moles of PCL were applied, and 709 % at 4.5 moles. Adhesive strength was 2.887 kgf / cm when 3 moles of PCL was applied and 0.998 kgf / cm when 4.5 moles were applied.

본 연구에서는 에틸아세테이트와 피페라진을 적용한 가죽 표면 코팅제로 사용할 수용성 폴리우레탄의 합성을 위해 poly(tetramethylene ether) glycol(PTMG)를 기반으로 isoporon diisocyanate (IPDI)와 dimethylolbutanoic acid(DMBA)의 반응을 통해 프리폴리머를 합성하였다. 이후 수분산시킨 수지에 피페라진을 0.01M, 0.03M, 0.05M, 0.07M을 쇄연장 반응을 해서 각각의 인장강도, 연신율, CV(cyclic voltammetry), 내용제성 분석을 실시했다. 준비된 시료의 인장강도는 피페라진 함량 0.07M일 때 5.422 kgf/㎟ 로 측정되었으며, 연신율을 측정한 결과 피페라진이 0.01M 일 때 587 %로 측정되었다. 내용제성 분석결과 피페라진 함량과 상관없이 동등한 내용제성으로 측정되었으며, CV 측정을 통해 피페라진 함량에 따라 산화환원전위가 변화되는 것을 확인 할 수 있었다.

Buffalo leather 표면 코팅에 사용된 폴리우레탄 수지에 glycerol의 함유를 mole % 비로 달리 하면서 첨가 하였다. 합성된 폴리우레탄 수지의 기계적 특성은 SEM, FT-IR, UTM 등을 이용하여 측정 하였다. 친환경적인 고분자 수지의 관심이 고조됨에 따라 용제의 사용을 최소화한 buffalo leather 코팅에 사용되는 수분산 수지를 합성하였다. 지방족 3가 알콜인 glycerol의 mole % 비가 증가함에 따라 내마모 도, 인장강도가 감소함을 알 수 있었다. 반대로 연신율, 내굴곡 물성은 증가함을 알 수 있었다. Toluene 을 이용한 내용제성 물성측정 결과에는 glycerol의 mole % 증가에 따른 물성 증감 효과는 없었다.

Vegetable leather 표면 코팅에 사용된 폴리우레탄 수지는 glycerol의 함유를 mole% 비로 달 리하면서 합성하였다. 합성된 폴리우레탄 수지의 기계적 특성은 SEM, FT-IR, UTM 등을 이용하여 측 정하였다. 친환경적인 고분자 수지의 관심이 고조됨에 따라 용제의 사용을 최소화한 vegetable leather 코팅에 사용되는 수분산 수지를 합성하였다. 지방족 3가 알콜인 glycerol의 mole% 비가 증가함에 따라 내마모도, 인장강도가 증가함을 알 수 있었다. 반대로 연신율, 내굴곡 물성은 감소함을 알 수 있었다. Toluene을 이용한 내용제성 물성측정 결과에는 glycerol의 mole% 증가에 따른 물성 증감 효과는 없었 다.