        1.
        2016.11 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        In order to identify changes in the nature of the particles due to changes in the inflow rate of the raw material solution, the present study was intended to prepare nano-sized cobalt oxide (Co3O4) powder with an average particle size of 50 nm or less by spray pyrolysis reaction using raw cobalt chloride solution. As the inflow rate of the raw material solution increased, droplets formed by the pyrolysis reaction showed more divided form and the particle size distribution was more uneven. As the inflow rate of the solution increased from 2 to 10 ml/min, the average particle size of the formed particles increased from about 25 nm to 40 nm, while the average particle size did not show significant changes when the inflow rate increased from 10 to 50 ml/min. XRD analysis showed that the intensity of the XRD peaks increased remarkably when the inflow rate of the solution increased from 2 to 10 ml/min. On the other hand, the peak intensity stayed almost constant when the inflow rate increased from 10 to 50 ml/min. With the increase in the inflow rate from 2 to 10 ml/min, the specific surface area of the particles decreased by approximately 20 %. On the contrary, the specific surface area stayed constant when the inflow rate increased from 10 to 50 ml/min.
        4,000원
        2.
        2014.06 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        Using the spray pyrolysis process, nano-sized cobalt oxide powder with average particle size below 50 nm was prepared from cobalt chloride solution. The influences of the raw material solution on the properties of the powder formed examined. When the concentration of Co was low(20 g/L), the average particle size of the powder formed was roughly 20 nm, and the cohesion between these particles was significantly strong. When the concentration of Co increased to 100 g/L, the droplets nearly failed to exist in circular form and reflected a severely divided form. Furthermore, the average size of the particles formed was roughly 40 nm, and the particles reflected a polygonal form. When the solution was increased to nearly saturation level (Co at 200 g/L), the particle size distribution reflected significant unevenness due to severe droplet division while the surface also reflected significant unevenness. Furthermore, the average size of the particles formed increased significantly to 70 nm. The results of XRD analysis showed that the strength of the peaks reflected very little change when the concentration of Co was increased from 20 g/L to 50 g/L. Alternatively, when the concentration was increased to 100 g/L, the strength of the peaks increased compared to when the concentration was 50 g/L. However, when the concentration was increased to 200 g/L, the strength of the peaks failed to reflect significant change compared to when the concentration was 100 g/L. The specific surface area dramatically decreased by 30 % when the concentration of Co was increased from 20 g/L to 50 g/L. Alternatively, when the concentration of Co the solution increased to 100 g/L, the specific surface area decreased by roughly 15 %. Furthermore, when the concentration of Co was increased to nearly saturation level(200 g/L), the specific surface area decreased by roughly 35%.
        4,000원
        3.
        2014.01 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        In this study, nano-sized cobalt oxide powder with an average particle size below 50 nm was prepared from a cobalt chloride solution by the spray pyrolysis process. The influences of reaction temperature on the properties of the generated powder were examined. The average particle size of the particles formed based on the spray pyrolysis process at a reaction temperature of 700˚C is roughly 20 nm. Moreover, most of these particles cannot appear with an independent type, thereby coexisting in a droplet type. When the reaction temperature increases to 800˚C, the average particle size not only increases to roughly 40 nm but also shows a more dense structure while the ratio of particles which shows a polygonal form significantly increases. As the reaction temperature increases to 900˚C, the distribution of the particles is from roughly 70 nm to 100 nm, while most of the particle surface is more intricately close and forms a polygonal shape. When the reaction temperature increases to 1000˚C, the particle size distribution of the powder shows an existing form from 80 nm to at least 150 nm in an uneven form. As the reaction temperature increases, the XRD peak intensity gradually increases, yet the specific surface area gradually decreases.
        4,000원