The friction and wear characteristics of the rubber matrix composites filled with nano sized silica particles were investigated at ambient temperature by pin-on-disc friction test. The volume fraction of silica particles was 19%. The cumulative wear volume and wear rate of these materials on counterpart roughness were determined experimentally. The major failure mechanisms were lapping layers, deformation of matrix, ploughing, debonding of particles, fracture of particles and microcracking by scanning electric microscopy photograph of the tested surface. The cumulative wear volume showed a tendency to increase with increase of sliding distance. The wear rate of these composites tested indicated low value as increasing the sliding distance.

본 연구에서는 입자강화 복합재료(particle-reinforced composites)의 거동을 예측하기 위하여 Lee and Pyo(2007)에 의해 제안된 계면손상을 고려한 복합재료의 미세역학 탄성모델과 Karihaloo and Fu(1989)의 미세균열 생성모델을 결합하여, 보강입자의 계면손상(imperfect interface)과 기지 내 미세균열을 고려하여 탄성구성모델(constitutive model)의 거동해석을 수행하였다. 제안된 탄성구성모델의 적용성 검증과 주요손상변수가 거동예측에 미치는 영향을 알아보기 위해 일축 하중 하에서의 응력-변형률 관계를 수치적으로 나타내었다. 또한, 기존의 관련 실험결과와 본 해석결과와의 비교를 통하여 제안된 모델의 정확도를 검증하였다.