PURPOSES: This study aims to develop a repair material that can enhance pavement performance, inducing rapid traffic opening through early strength development and fast setting time by utilizing MgO-based patching materials for repairing road pavements. METHODS : To consider the applicability of MgO-based patching materials for repairing domestic road pavements, first, strength development and setting time of the materials were evaluated, based on MgO to KH2PO4 ratio, water to binder ratio, and addition ratio of retarder (Borax), by which the optimal mixture ratio of the developed material was obtained. To validate the performance of the developed material as a repair material, the strength(compressive strength and bonding strength) and durability (freezing, thawing, and chloride ion penetration resistance) was checked through testing, and its applicability was evaluated. RESULTS : The results showed that when an MgO-based patching material was used, the condensation time was reduced by 80%, and the compressive strength was enhanced by approximately 300%, as compared to existing cement-based repair materials. In addition, it was observed that the strength (compressive strength and bonding strength) and durability (freezing and thawing, and chloride ion penetration resistance) showed an excellent performance that satisfied the regulations. CONCLUSIONS : The results imply that an emergent repair/restoration could be covered by a rapid-hardening cement to meet the traffic limitation (i.e. the traffic restriction is only several hours for repair treatment). Furthermore, MgO-based patching materials can improve bonding strength and durability compared to existing repair materials.

다양한 원인에 의한 포장체에 손상이 발생하면 신속한 통행재개를 위한 급속보수가 필요하게 된다. 산화마그네슘인산염복합체의는 경화시간이 짧고, 조기 강도발현이 가능하여 급속보수재료로 적합한 특성을 갖고 있다. 연구에서는 경소마그네시아와 제1인산칼륨을 결합하여 보수재료로 개발하기 위하여 물-결합재(W/B)비, 마그네슘-인산염(M/P)비 등의 배합비를 조정하면서 경화와 강도특성을 평가하고자 하였다. 그리고 현장 적용시의 작업성을 확보하기 위하여 표준사와 일반모래에 따른 거동차이와 지연제별 특성을 평가하였다. 실험결과 물-결합재비는 35%내외와 마그네슘-인산염비는 1.0~1.2 내외가 강도측면에서 가장 적합한 것으로 분석되었다. W/B비 0.35, M/P비 1.2 변수에서 1일 강도 25.0MPa 이상 발현되어 조기 보수재료로서 활용가능성이 충분한 것으로 분석되었다. 작업시간 확보를 위해서는 붕산을 지연제로 사용하는 것이 적합한 것으로 나타났으며, 산화마그네슘의 순도는 90~95%내외가 경화시간 확보를 위해 효과적인 것으로 나타났다.