PURPOSES : The performance properties (indirect tensile strength, rutting resistance, and resilient modulus) of recycled aged CRM mixtures and their correlation with Superpave binder properties (viscosity, high failure temperature, G*sinδ, and stiffness) were investigated. METHODS: A series of Superpave binder tests was performed by using a rotational viscometer, DSR, and BBR to evaluate the performance properties. In addition, the CRM mixes were artificially aged through accelerated aging processes, and their properties were evaluated. The correlation between the properties of recycled aged CRM binders and the engineering properties of recycled aged CRM mixtures was experimentally determined. RESULTS : The rut depth values decreased and the ITS values increased with increasing high failure temperature. In general, the resilient modulus properties seemed to be poorly correlated with the high-temperature values, regardless of the aggregate source. CONCLUSIONS: The recycled aged CRM binders and mixtures can lead to satisfactory performance, and the properties of these binders are strongly correlated with the engineering properties of the mixtures.

본 연구는 PG 등급에 따른 아스팔트 혼합물의 변형강도(SD)와 소성변형 저항성의 상관관계를 규명하고자 하였다. 마샬배합설계는 포장의 공용성과의 상관성이 낮아 본 연구에서는 수퍼페이브 배합설계를 통하여 혼합물을 제조하고 소성변형 특성과 상관성이 높은 역학적 특성을 측정하기 위해 개발된 변형강도(SD), 그리고 휠 트랙킹 시험으로 최종침하깊이(DR)와 동적안정도(DS)를 구하였다. 또한 변형강도 측정시 4(1.0) 하중봉을 사용하였으며 60℃에서 수침시간을 30, 40, 50분으로 변화시켜 가며 바인더 등급에 따라 SD를 측정하여 수침시간별 SD와 DS. SD와 DR의 상관관계를 분석하였다. 그 결과 수침시간 30분의 경우가 가장 높은 R2을 나타냈으며 SD가 수퍼페이브 혼합물에서도 소성변형저항성과 아주 밀접한 상관관계를 보임을 알 수 있었다.