        2018.12 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Nitrogen-doped carbons have attracted much attention due to their novel application in relation to gas storage. In this study, nitrogen-doped porous carbons were synthesized using SBA-15 as a template, polypyrrole as the carbon and nitrogen precursor, and KOH as an activating agent. The effect of the activation temperature (600–850°C) on the CO2 adsorption capacity of the obtained porous carbons was studied. Characterization of the resulting carbons showed that they were micro-/meso-porous carbon materials with a well-developed pore structure that varied with the activation temperature. The highest surface area of 1488 m2 g–1 was achieved at an activation temperature of 800°C (AC-800). The nitrogen content of the activated carbon decreased from 4.74 to 1.39 wt% with an increase in the activation temperature from 600 to 850°C. This shows that nitrogen is oxidized and more easily removed than carbon during the activation process, which indicates that C-N bonds are more easily ruptured at higher temperatures. Furthermore, CO2 adsorption isotherms showed that AC-800 exhibited the best CO2 adsorption capacity of 110 mg g–1 at 298 K and 1 bar.
        4,000원