본 연구에서는 폴리비닐알콜(PVA)와 폴리프로필렌글리콜(PPG)기반의 창상피복용 수분산 폴리우레탄수지를 합성하였으며, 시료의 물리적 특성을 필름 시료와 피혁(Full-Grain) 표면에 코팅을 하여 물리적 특성 변화를 연구하였다. 인장강도의 경우 PVA가장 적게 반응된 PUD-PA1 2.00 kgf/㎟ 으로 가장 높은 저항성을 보였으며. 마찬가지로 연실율은 PVA가장 적게 반응된 PUD-PA1가 554%로 높게 측정되었다. 내마모성 측정 결과 PVA 반응이 증가함에 따라 표면의 강도나 낮게 36.77 ㎎.loss로 감소 됨을 알수 있었다.

In this study, the polyurethane resin was synthesized by applying PTMG and DMBA of different composition ratios for the synthesis of water-dispersible polyurethane used in wound coating resin. The varying properties of the synthesized water-dispersible polyurethane were measured through tensile strength, elongation, and abrasion resistance analysis. As for the tensile strength measurement result according to the PTMG content, the sample with the highest reaction molar ratio was measured as 1.08 kgf/mm2 and the elongation was measured as 520%. As for the tensile strength result according to the DMBA content, the sample with the highest reaction molar ratio was measured as 0.51 kgf/mm2, and the elongation was measured as 435%. The degree of surface destruction by the abrasion resistance measurement was visually confirmed through SEM.