In this study, Early compressive strength analysis of low carbon mortar using industrial byproducts and describes relationships between strength property and CO2 indices to evaluate eco-efficient of low carbon binder mortar. Based on the results, this study is to give fundamental data for ability of eco-efficient low carbon binder.

The purpose of this study is to investigate the field application of Permeability recycled asphalt using Waste Asphalt Concrete and Resin. After the test construction, it was not cause problem, such as this stripping, falling and crack of pavement. Also, it was confirmed to be performance of equal or higher than of existing technology.

The purpose of this study is to investigate correation between semi-adiabatic temperature and adiabatic temperature rise of ordinary portland cement(OPC) and ternary blended cement(TBC). And concrete adiabatic temperature rise factor was estimated by semi-hydration heat analysis test.

최근 도로의 개･보수 공사 뿐만 아니라 도시가스, 상수도 및 오폐수 관거 등의 교체공사로 인하여 건설 산업 부산물 중에 폐아스콘의 발생량이 상당한 부분을 차지하고 있다. 이러한 폐아스콘의 처리 및 건설공사 골재부족 현상 심각성이 대두됨에 따라 자원순환을 위한 정부의 패러다임 전환 정책이 강화되고 있다. 한편 실온에서 사용이 가능한 MMA(Methyl Methacrylate) 수지를 이용한 투수성 재생아스팔트의 역학적 성능에 대한 기초실험을 실시한 결과 MMA 수지를 이용한 투수성 재생아스팔트의 마샬안정도 및 흐름값 모두 KS 기준을 만족하는 것을 확인하였다. 따라서, 본 연구에서는 폐아스콘을 처리한 순환골재와 MMA 수지를 이용한 투수성 재생아스팔트의 내구성능을 확인하기 위하여 마모저항성 및 동적안정도에 대하여 분석하였다. 배합조건에 따른 마모저항성 시험결과, 모든 배합조건에서 시험체의 질량 손실률이 18%이하로 나타났다. 투수성 재생아스팔트의 경우 골재와 골재 사이의 결합재 및 공시체의 수밀한 정도에 의해 칸타브로 손실률의 차이가 크게 발생하나, 본 실험에서의 제조된 공시체는 모두 우수한 내마모성을 나타내는 것으로 나타났다. 투수성 재생아스팔트의 동적안정도를 평가하기 위하여, 상온 25℃에서 휠트래킹 시험방법으로 동적안정도를 평가한 결과, PCRA-1(L사 MMA)의 경우가 PCRA-2(N사 MMA)의 경우 보다 완만한 변형률을 나타내었으며 최종 변형량의 차이가 약 0.44 ~ 3.37mm의 차이가 나타났다. KS 규격에 준하는 시험체 3개의 평균값으로 산정된 변형량의 차이는 약 1.75mm로서 PCRA-2의 시험체가 약 1.94배 더 큰 변형량을 나타내었다. 한편 PCRA-1의 시험체는 약 5분까지는 급격히 중앙부 처짐량이 증가하는 경향을 나타났으나, 그 후 60분까지 서서히 처짐량이 증가하였다. 따라서, PCRA-1의 배합이 변형에 대한 저항성이 우수한 것으로 판단된다.

In this study, Analyzed characteristic about permeability cold-mixed recycled asphalt concrete using waste asphalt concrete and MMA. As a result, porosity was 20.4%, Water permeability coefficient was 0.94cm/sec and Skid Resistance test was 50BPN

This study was carried out to investigate the effect of simple hydroponic culture in cultivation of grafted cactus. The results obtained are as follows: Growth indexes of grafted cactus cultivars, such as scion diameter, fresh weight, and scion hardness were improved in simple hydroponic culture compared with soil culture regardless of cultivars. Stem rot and rate of non-graft take were lower in simple hydroponic culture than in soil culture, but no significant difference was monitored between cultivars. Time for harvesting was fast in simple hydroponic culture compared with soil culture. Marketable yield increased in simple hydroponic culture.

본 연구는 나리 주요 품종의 종간교잡에서 생기는 삭과의 배 유 퇴화방지와 미숙배 형성 시 발생하는 이상증상을 경감하기 위해 나리 종간교잡계통의 자방배양 했을 때 cytokinin 첨가가 신초형성에 미치는 영향을 구명하고자 하였다. FO계통은 BA 2.0 ㎎/L에서 신초 발생율이 18%로 가장 효과적이었고, BA 3.0 ㎎/L와 5.0 ㎎/L에서는 12%로 다소 저조한 결과였다. TDZ 첨가 의 경우는 대조구와 같거나 비슷한 경향이었다. FA계통은 TDZ 첨가 시 대체적으로 신초형성율이 높았고 0.3 ㎎/L 처리가 효과 적이었다. 반면 BA를 첨가한 배지에서는 14.3%에서 15.7%로 대 조구와 큰 차이가 없었다. FLA계통에서 신초발생율은 생장조 절제에 의해 증가되었으나 대조구 20%와 비교했을 때 BA 20~ 24%, TDZ 22~24%로 처리효과는 미미하였다.

In this study, Analyzed characteristic about permeability cold-mixed recycled asphalt concrete using waste asphalt concrete and MMA. As a result, porosity was 19.4% and permeability coefficient was 0.4cm/sec. Marshall stability test had the highest MMA 4% and a hardener 3%.

최근 도심지의 노후 된 포장 재정비 및 지하매설물 굴착 복구로 인한 폐아스콘 발생량이 지속적으로 증가하고 있으며, 이러한 건설폐기물 처리의 심각성이 대두됨에 따라 자원순환을 위한 정부의 패러다임 전환 정책이 강화되고 이에 따른 산업인프라 구축이 활발히 진행되고 있다. 한편 폐아스콘 순환골재를 활용한 투수성 재생 아스콘 제조를 통해 탄소배출량 저감, 지하수자원 보존 및 집중호우로 인한 도심지 침수 방지에 효과적일 것으로 예상된다. 따라서 본 연구에서는 투수성 재생아스팔트 혼합물의 제조 및 역학적 특성 규명에 앞서 폐아스콘순환골재의 물리적 특성을 분석하였다. 본 연구에서 사용되는 폐아스콘 순환골재는 G사에서 처리 및 생산된 골재로서 순환골재의 입도 크기별로 25~13mm, 13~8mm 및 8mm 이하의 것으로 분류하여 사용하였다. 25mm이하 폐아스콘 순환골재의 물리적 성질을 KS F 2503 ｢굵은골재의 밀도 및 흡수율 시험｣에 준하여 분석한 결과 밀도 및 흡수율이 각각 2.62 g/cm3, 1.45%로 나타났다. 폐아스콘 순환골재의 품질은 KS F 2572 ｢아스팔트 콘크리트용 순환골재｣에 준하여 실험하였으며, 구재아스팔트 함량 4.43%, 구재아스팔트 침입도(25℃, 1/10mm) 21, 씻기 시험에서 손실되는 양 1.0%, 유기이물질 0.07%, 무기이물질 0.11% 함유하는 것으로 나타나 아스팔트 콘크리트용 순환골재 품질규격에 적합한 것으로 확인되었다. 또한 폐아스콘 순환골재의 체가름시험 결과 골재입도는 25~13mm에서 25mm 100%, 20mm 85%, 13mm 72.5%, 10mm 54.6%, 5.0mm 39.6%, 2.5mm 27.3%, 0.6mm 15.9%, 0.3mm 11.5%, 0.15mm 7.3%, 0.08mm 2.8%, 골재입도 13~8mm에서 25~13mm 100%, 10mm 81.4%, 5.0mm 30.9%, 2.5mm 23.7%, 0.6mm 15.3%, 0.3mm 11.7%, 0.15mm 7.8%, 0.08mm 3.4%, 골재입도 8mm이하에서 25~10mm 100%, 5.0mm 93%, 2.5mm 74.5%, 0.6mm 41.9%, 0.3mm 29.6%, 0.15mm 19.1%, 0.08mm 6.9%의 체통과율이 확인되었으며, 향후 투수성 재생아스콘의 골재로 사용하기 위하여 입도별에 따른 투수성능 및 혼합물의 역학적 특성을 평가하여야 할 것으로 판단된다.

The purpose of this study is to investigate the field application of cold-mixed recycled asphalt using cementless binder. After the test construction, it was not cause problem, such as this stripping, falling and crack of pavement. Also, it was confirmed to be performance of equal or higher than of existing technology.

The purpose of this experimental study is to investigate the influence of chemical resistance of concrete using KOH and Non-sintered binder. As a result, concrete using KOH and Non-sintered binder was confirmed to be superior than ordinary of concrete chemical resistance.

경제성장과 더불어 산업발전이 급격하게 이루어짐에 따라 산업폐기물이 나날이 증대되어 대기 중의 환경오염 및 폐기물의 무단방치 및 불법매립 등의 환경오염 문제가 사회적인 심각한 문제점으로 대두되고 있다. 수많은 산업폐기물 중 주물산업에서 발생하는 폐주물사는 연간 발생량이 약 300만 톤이며 이를 대부분 야적･매립함으로써 이에 따른 2차 환경오염을 발생시키고 있다. 이러한 폐주물사를 재활용하는 방안으로 건설 산업에서 시멘트나 잔골재의 대체 재료로서 재활용하는 방안으로 연구가 요구되고 있다. 따라서 본 연구에서 산업부산물인 폐주물사의 첨가에 따른 시멘트 모르타르의 흐름값 및 강도특성에 대한 검토를 실시하였으며, 이를 위하여 결합재와 주문진 표준사를 1:2.45, W/B=53%로 설정하고 폐주물사를 시멘트 2 ~ 40%, 잔골재 10 ~ 50% 대체 혼입하여 공시체를 제작하였다. 실험에 사용한 폐주물사의 밀도는 2.42 g/cm³로 시멘트나 잔골재에 비해 작은 편이며, 폐주물사를 시멘트 대체재로 혼입한 모르타르의 흐름값 측정결과 혼입량이 0%, 2%, 4%, 6%, 8%, 10%, 20%, 30%, 40%인 경우 각각 152 mm, 146 mm, 145 mm, 143 mm, 138 mm, 136 mm, 120 mm, 114 mm, 112 mm로 최대 26% 감소하는 경향을 나타내었다. 그리고 제작된 공시체를 20℃로 양생하여 7일 압축강도를 측정한 결과 혼입량이 0%인 경우에 비하여 8%, 40% 혼입하였을 때 각각 18%, 65% 감소한 6.28MPa, 7.90MPa이며, 10% 이상 혼입하였을 때 강도가 급격히 감소하는 경향을 나타내었다. 잔골재 일부를 폐주물사로 대체 혼입한 모르타르의 흐름값 측정결과 혼입량이 0%, 20%, 40%인 경우 각각 152 mm, 134 mm, 115 mm로 최대 24%감소하는 경향을 나타내었다. 또한 제작된 공시체를 20℃로 양생하여 3일, 7일 압축강도를 측정한 결과 혼입량이 0%인 경우에 비하여 40% 혼입 하였을 때 각각 10%, 12% 감소하여 20.13 MPa, 17.41 MPa로 나타났다. 따라서, 폐주물사를 콘크리트 재료의 대체재로 사용할 경우 입도분포를 고려하여 잔골재의 대체재로 사용하는 것이 효과적인 것으로 판단된다.

The purpose of this study is to investigate the characteristics of compressive strength and workability according to the NaOH and KOH addition method as powder of mortar which is made of Non-sintered binder for the reuse of resources and the CO2 reduction

This study was performed an evaluation of physical & mechanical properties of mortar by Non-Sintered binder of ball milling time according to fineness.

본 연구에서는 풍력발전기 타워의 효과적인 상태 모니터링을 위하여 타워의 고유진동수 및 모드형상을 이용한 손상추정기법을 제안하였다. 풍력발전기에 대한 동력학 시뮬레이션 프로그램을 이용하여 타워의 거동을 시뮬레이션하고 결과를 이용하여 타워의 모드특성을 추정하였다. 다양한 손상에 의한 타워의 고유진동수와 모드형상의 변화를 모드특성 추정 프로그램을 이용하여 해석적으로 구하여 훈련패턴을 생성하고 이를 이용하여 신경망을 훈련시켰다. 복수 손상 경우를 포함한 10가지 손상경우에 대한 모드특성을 훈련된 신경망에 입력하여 손상을 추정하였으며, 모든 손상 경우에 대하여 비교적 정확하게 손상위치와 손상정도를 판정할 수 있었다. 단, 미소 손상의 경우 손상정도가 약간 과소평가되는 경향을 보였으나 손상위치는 합리적으로 추정됨을 알 수 있었다. 향후, 미소 손상 추정결과의 정확성을 개선하고, 실험을 통하여 제안된 기법을 검증할 계획이다.

본 연구에서는 효과적인 풍력발전기 블레이드의 상태 모니터링을 위하여 대표적 손상형태 중 하나인 로터의 질량 불균형으로 인한 이상상태를 감지할 수 있는 기법을 제안하였다. 이를 위하여 수평축 3-블레이드 풍력발전기를 대상으로, 블레이드 1개의 질량을 증가시키면서 로터의 질량 불균형 조건을 구현한 후 전체 풍력발전기에 대한 동력학 시뮬레이션을 수행하였다. 질량불균형이 발생하면 부가질량에 의한 원심력에 의하여 나셀의 로터 회전축에 대한 횡방향 진동이 발생하고, 부가 질량의 크기가커질수록 나셀 횡방향 진동의 진폭이 거의 선형적으로 증가함을 알 수 있었다.

본 논문에서 3DARModeler 라는 증강현실 환경에서의 3D 모델링 시스템에 대해서 제시 한다. 이 시스템은 3D 객체(모델)를 만들기 위해 객체 호출, 텍스쳐 적용, 애니메이션, 광원추정, 그림자 등의 기능들이 포함된 간단한 3D Studio Max라고 볼 수 있다. 3DARModeler는 3D 모델을 만들기 위한 효과적이고 편리한 상호작용 방법들을 제시한다. 3DARModeler 시스템의 주사용자는 컴퓨터 그래픽, 모델링 기술에 관한 많은 지식을 갖추지 않은 비전문가들을 대상으로 한다. 사용자들은 기본 객체를 선택, 객체들의 속성 부여, 여러 객체들의 결합을 통하는 방법으로 사용자가 실세계에서 직접 모델링을 하는 것과 같이 간단하고 직관적인 방법의 모델링을 가능하도록 한다.

리트벨트 분석법과 저온에서 측정한 방사광 가속기 분말회절 자료를 이용하여 CFC-13 (CF3Cl; chlorotrifluoromethane) 분자체가 흡착된 제올라이트 Na,K-LSX (low-silica X or synthetic faujasite)의 구조분석을 수행하였으며, supercage 내의 6-ring주변에 CFC-13 분자체의 불소 원자와 LSX 제올라이트의 나트륨 양이온 간의 결합이 일어남을 확인하였다.