The effect of β-heat treatment on th microstructure, mechanical properties and texture in the nuclear fuel cladding of Zircaloy-4 tubes was chosen at 1000, 1100 and 1200˚C, and the tubes were heat-treated by a high frequency vacuum induction furnace. Morphology of the second phase particles and α-grain of as-received tubes were markedly changed by heat treatment. The average sizes of second phase particles of as-received and β-heat treated tubes were 0.1μm and 0.076μm, respectively. However, the average sizes of second phase particles were not much changed in the β-heated temperatures. With increasing heat treatment temperatures, the 0.2% yield strength and the hoop strength were decreased because of changes in preferred orientation as will as α-plate width. Heat treated Zircaloy-4 tubes exhibited texture changes but the preferred orientation of grains still remained.

자동차용 캠 샤프트의 표면경화를 위해 TiG 용접공정에 의한 재용융처리가 실시되었다. 재용융처리는 캠축에 평행한 방향으로 행하여졌다. 캠 샤프트 소재의 조직은 편상의 흑연과 퍼얼라이트의 회주철 조직으로 구성되어 있으나 재용융 처리후 미세한 퍼얼라이트 및 세멘타이트와 구상 오스테나이트의 레데브라이트 조직으로 변화하였다. 캠 샤프트 모재의경도는 HRc 25~28에서 재용융 처리후에는 HRg 53~55정도로 증가하였다. 다층 용융 처리시 비드가 겹치는 경계에서 검은띠가 관찰되었는데 이 검은띠는 흑연으로 판명되었다. 이 검은띠는 전층의 레데브라이트 조직이 변태된 것으로 주로 세멘타이트와 기지조직의 경계에서 생성되었다. 고밀도 에너지인 레이저 용융처리시에도 재흑연화 현상은 TIG의 경우처럼 관찰되었다. 재흑연화 현상의 확인을 위해서 Gleeble 1500을 이용하여 1100˚C와 1000˚C에서 0.5, 1, 3, 5 및 10초동안 유지한 모의실험을 하였다. 1000˚C에서 0.5초 유지했을 때도 흑연이 발견된 것으로 보아 재흑연화 현상은 어떠한 재용융 처리 공정을 사용하더라도 피할 수 없는 현상임을 확인할 수 있다.