The purpose of this study was to evaluate the tensile fracture energy absorption capacity of hybrid fiber reinforced cement composite by strain rate. Experiment result, it was confirmed that PVA suppressed the microcrack around the HSF at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the HSF.

CFRP (Carbon Fiber Reinforced Plastic) has high tensile strength, light weight, and excellent corrosion resistance, so it is used for construction such as seismic reinforcement and explosion proof in construction area. Dynamic loads, such as earthquakes and explosions, cause rapid deformation of the material and the material behaves differently from its static condition. Therefore, in this study, tensile tests of CFRP were conducted under static and dynamic loads, and the tensile performance of was evaluated according to the strain rate.

급속공사 현장에 사용되는 속경성 보수모르타르의 내구성능 증진을 위해 사용재료의 물리적 성능을 평가하였다. 이를 위해 염화물 확산 억제 성능을 보유한 페로니켈 수쇄슬래그 잔골재와 급결제, EVA계 폴리머를 모르타르에 치환시켜 급결성능과 기초적 성능을 평가하였다. 그 결과 FNS잔골재 및 RS잔골재 사용에 따른 압축강도, 휨강도, 부착강도가 증가되었다. 속경성 폴리머 모르타르의 염화물 이온 촉진시험의 결과 FNS를 50%이하 사용 시 재령 7일에서 재령 28일간 염화물 억제 성능이 유지되었으며, FNS잔골재 및 RS잔골재 사용에 따른 내구성 저하는 발견되지 않았으나, 건축 및 토목용 대체골재로 사용하는데 경제성 및 장기 내구성에 대한 추가 검토가 필요할 것으로 판단된다.

본 연구에서는 비정질강섬유의 혼입이 초고강도콘크리트의 폭렬특성에 미치는 영향이 실험적으로 검토되었다. 콘크리트는 압축강도 100과 150 MPa의 초고강도콘크리트가 사용되었다. 폴리프로필렌섬유는 0.15 vol%, 비정질강섬유는 0.3 및 0.5 vol%가 혼입되었다. 시험체는 콘크리트의 압축강도와 섬유혼입 조건에 따라 6수준이 제작되었고, ISO-834 가열곡선에 의해 가열되었다. 결과로써 폴리프로필렌섬유와 비정질강섬유가 혼입된 초고강도콘크리트의 폭렬제어에 있어서는 용융된 폴리프로필렌섬유가 형성하는 공극네트워크를 통해 수증기가 이동하는 효과가 지배적인 것으로 나타났다. 또한, 비정질강섬유 0.3v ol% 혼입률에서는 폭렬제어에 큰 영향을 미치지 않지만, 0.5 vol%의 비정질강섬유가 혼입될 경우에는 수증기가 이동할 수 있는 균열의 발생이 억제됨으로써 콘크리트 폭렬의 원인으로 지적되고 있는 수분막힘층(moisture clog)가 형성될 가능성이 높은 것을 확인할 수 있었다.

The purpose of this study was to evaluate the direct tensile fracture behavior of steel fiber hybrid reinforced cement composite by strain rate. Experiment result, it was confirmed that SSF suppressed the microcrack around the HSF at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the HSF.

In this study, it evaluate the Local damage properties of amorphous metallic fiber reinforced cement composite by different fiber length. 30mm and 15mm length of amorphous metallic fiber was reinforced and fiber volume fraction was set to 1.0, 1.5 vol.%. Flexural test and high speed projectile impact test was performed. As as result, 30mm length of specimen showed more good flexural and impact resistance performance compared to 15mm length of specimen.

해양 콘크리트 구조물 중 침지대에 위치한 구조물은 수심이 10 m 깊어질수록 1 atm의 정수압을 받아 염화물이온 침투가 촉진될 가능성이 있다. 본 연구에서는 정수압이 해양콘크리트의 염화물이온침투에 미치는 영향과 원인을 평가하기 위하여 보통 포틀랜드 시멘트와 고로슬래그 시멘트를 활용한 콘크리트를 각각 1, 6 atm의 정수압과 인공해수에 노출시켜 깊이별 수용성 염화물량과 미세구조 분석을 실시하였다. 측정결과 6 atm의 정수압을 받는 콘크리트는 표면 염화물이온 농도가 급격하게 상승하며, 깊이별 수용성 염화물량이 증가하는 경향을 나타내었다. 또한, 정수압을 받은 콘크리트는 5~100 nm에 해당하는 모세관공극이 증가하는 경향을 나타내었다.

In this study, it evaluate the impact resistance of UHPC by repeated impact. smooth steel fiber and polyvinyl alcohol fiber were reinforced in UHPC respectively. Overall, the impact resistance of the specimens reinforced with 0.4vol.% PVA fiber was high, and the crater diameter was small in specimens using 13mm fiber.

The purpose of this study was to evaluate the mechanical properties and bond performance of epoxy paint containing graphene materials. Experiment result, it was confirmed that graphene materials are effective to improve the mechanical properties of the epoxy paint, but it is not effective to improve the bond performance.

In this study, it evaluate the electromagnetic pulse shielding performance of fiber reinforced cement composite by Fiber type. Hooked-ended steel fiber, Smooth steel fiber and Amorphous metallic fiber were reinforced 2.0 vol.% in cement composites respectively. The electromagnetic pulse shielding performance was evaluated by MIL-STD-188-125-1.

The purpose of this study was to evaluate the direct tensile fracture behavior of fiber hybrid reinforced cement composite by strain rate. Experiment result, it was confirmed that PVA suppressed the microcrack around the steel fiber at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the steel fiber.

In this study, the fiber blending ratio and strain rate effect on the tensile behavior of hybrid fiber reinforced cement composite was evaluated. Hooked steel fiber and polyvinyl alcohol fiber were used for reinforcing fiber. The fiber blending ratio of HSF+PVA were 1.5+0.5, 1.0+1.0 and 0.5+1.5vol.%. As a results, the tensile strength, strain capacity and fracture toughness of the hooked steel fiber reinforced cement composites were improved by the increase of the bond strength of the fiber and the matrix according to increase of strain rate. However, the tensile stress sharply decreased after the peak stress because of the decrease in the number of straightened pull-out fibers by micro cracks in the matrix around hooked steel fiber. On the other hand, PVA fiber showed cut-off fracture at strain rate 10-6/s with multiple cracks. However, at the strain rate 101/s, the multiple cracks and strain capacity were decreased because of the pull-out fracture of PVA fiber. The HSF1.5PVA0.5 shown the highest tensile strength because the PVA fiber suppressed the micro cracks in the matrix around the hooked steel fiber and improved the pull-out resistance of hooked steel fiber. Thus, DIF of strain capacity and fracture toughness of HSF1.5PVA were greatly improved. In addition, the synergistic response of fracture toughness was positive because the tensile stress was slowly decreased after the peak stress by improvement of the pull-out resistance of hooked steel fiber at strain rate 101/s

α형 반수석고는 생산방법이 복잡하고, 대량 연속 생산이 곤란하며, 재료 단가가 높기 때문에 건설재료로써 활용범위가 크지 않았으 나, 최근 화력발전소의 배연탈황석고를 활용하여 경제적으로 α형 반수석고를 제조하는 기술이 실용화되고 있다. 이에 본 연구에서는 응결 시 작 시간이 빠르고 재령 초기 팽창변형이 발생하는 α형 반수석고의 특징에 주목하여, α형 반수석고를 10, 20, 30 wt.% 치환한 보통포틀랜드시멘 트 및 고로슬래그시멘트 모르타르를 제조한 후 응결 및 압축강도 특성, 건조수축을 검토하였다. 실험 결과, α형 반수석고의 치환율이 증가할수 록 보통포틀랜드시멘트 모르타르 및 고로슬래그시멘트 모르타르의 초결시간이 빨라지는 경향을 확인할 수 있었다. 또한, 보통포틀랜드시멘 트 모르타르와 고로슬래그시멘트 모르타르 모두 α형 반수석고의 치환율이 증가할수록 압축강도가 저하되는 경향을 보였으며, 보통포틀랜드 시멘트보다 고로슬래그시멘트에서 α형 반수석고의 압축강도 발현이 유리한 것으로 나타났다. 한편, α형 반수석고를 치환한 모르타르의 경우 α형 반수석고의 혼입에 의해 생성된 에트링가이트 침상결정의 성장압에 의해 초기재령에서 수축변형이 저감되는 것을 확인할 수 있었으며, 초 기 재령에서 수축변형의 억제 효과는 분명하지만, 재령이 지남에 따라 α형 반수석고를 치환하지 않은 조건과 변형의 차이는 다시 감소하는 경 향을 보였다. 따라서 α형 반수석고를 모르타르에 적용할 경우 강도는 다소 저하하지만, 응결 촉진 및 수축변형 억제에 큰 효과가 있기 때문에 건설재료로써 활용 가치가 높을 것으로 판단된다.

In this study, it evaluate the electrical conductivity of fiber reinforced cement composite by Fiber type. Hooked-ended steel fiber, Smooth steel fiber and Amorphous metallic fiber were reinforced 2.0 vol.% in cement composites respectively. The electrical conductivity was evaluated by calculating the electrical resistivity of each specimen after measuring the electrical resistance.

The degradation of concrete exposed to high temperature was evaluated by applying ultrasonic pulse velocity evaluation method which is one of the nondestructive tests of concrete. As a result, it is difficult to distinguish compressive strength of concrete and estimate residual compressive strength of concrete. However, it was confirmed that the higher the heating temperature, the lower the compressive strength and ultrasonic velocity of the concrete.

The purpose of this study was to evaluate the tensile fracture behavior of fiber hybrid reinforced cement composite according to the strain rate. Experiment result, it was confirmed that the number of cracks and the strain capacity tended to decrease with increasing PVA fiber volume fraction at the strain rate of 101/s.

As a result of evaluating the spalling properties using a restrained ring-type concrete specimen, in the case of rapid heating, the water vapor pressure rapidly rise and the surface spalling is repeated. In the case of low-speed heating, The water vapor pressure accumulated in the concrete exceeded the limit, and explosive spalling occurred inside.

본 연구에서는 유압식 급속재하 시험 장치를 제작하여 변형 속도에 따른 후크형 강섬유 및 폴리아미드 섬유보강 시멘트 복합체의 압축강도 및 인장강도 특성을 평가하였다. 그 결과, 변형 속도가 증가함에 따라 압축강도, 최대 응력 점에서의 변형 및 탄성계수는 증가하였으 며, 섬유 종류 및 혼입률은 변형 속도에 의한 압축강도의 영향은 크지 않았다. 본 연구에서 평가된 압축강도의 DIF는 CEB-FIP model code 2010 에 비해 상회하였으며, ACI-349의 예측값과 유사한 경향이 나타났다. 인장특성의 경우에도 변형 속도가 증가함에 따라 인장강도와 변형능력 이 크게 향상되었다. 후크형 강섬유보강 시멘트 복합체는 변형 속도가 증가함에 따라 섬유와 매트릭스의 부착력이 증가하는 것에 의해 인장강 도와 변형능력이 크게 향상되었으며, 섬유가 매트릭스로부터 인발되는 파괴 특성이 나타났다. 한편, 폴리아미드 섬유보강 시멘트 복합체의 경 우 섬유와 매트릭스의 부착력이 크기 때문에 섬유가 매트릭스로부터 인발되지 않고 끊어지는 파괴 특성이 나타났으며, 폴리아미드 섬유보강 시멘트 복합체의 인장특성에 대한 변형 속도 효과는 섬유의 인장강도에 큰 영향을 받는 것으로 판단되었다. 이러한 결과로부터 폴리아미드 섬 유보강 시멘트 복합체의 인장강도에 대한 변형 속도의 효과는 후크형 강섬유의 부착력에 대한 민감도 보다 큰 것으로 사료된다.

In this study, it evaluate the Impact fracture properties of fiber reinforced concrete and fiber reinforced cement composite. The types of fiber are Hooked-ended steel fiber and it was mixed 0.5, 1.0 vol.% in concrete and 1.0, 2.0 vol.% in cement composites. The Impact resistance performance was evaluated by measuring the fracture grade, penetration depth and scabbing depth

In this study, it evaluate the Impact fracture properties of fiber reinforced concrete and fiber reinforced cement composite. The types of fiber are Hooked-ended steel fiber and it was mixed 0.5, 1.0 vol.% in concrete and 1.0, 2.0 vol.% in cement composites. The Impact resistance performance was evaluated by measuring the fracture grade, penetration depth and scabbing depth