Thin films of Eu(TTA)3(phen), which was known to show red-light emitting properties, were deposited under various deposition condition. The thickness, surface morphology, and photoluminescence(PL) were measured with α-step profiler, Atomic Force Microscopy(AFM), and PL measurement apparatus. It was found that the thickness of Eu(TTA)3(phen) film can be controlled precisely by adjusting the amounts of Eu(TTA)3(phen) in the boat. As the thickness of these films increases, the surface roughness also increases. A structure of Al/Eu(TTA)3(phen)(850a)/TPD(600a)/ITO was fabricated, Electroluminescence(EL) spectrum of which shows the peak at the wavelength of 618nm.

Tris(8-hydroxyquinoline)-aluminum complex(AlQ3) having greenish luminescent characteristics was synthesized and it was confirmed with UV-Vis absorption spectroscopy, elemental analysis, and FT-IR spectroscopy that AlQ3 was successfully synthesized. Thin films of AlQ3 having multilayer structure were prepared by spin coating method and vacuum evaporation technique. Photopluminescent characteristics of these films were investigated by Luminescence spectroscopy and Current-Voltage(I-V) characteristics of these films were also investigated.

Ultra-thin films of poly[2-[4-(9-(10-phenyl)anthracenyl)phenoxy)hexyloxy]]-1,4-phenylenevinyleylene(PAHPV) were prepare-d on the hydrophilic ITO substrate by Langmuir-Blodgett(LB) technique. λmax in the photoluminescence spectrum of these films was 458nm at the excitation wavelength of 365nm before thermal treatment, which comes from diphenylanthracene side chain of PAHPV. It was also confirmed with UV-Vis spectrometer that ultra-thin LB films of PAHPV precursor polymer were prepared well. After thermal treatment for conjugation of PAHPV precursor polymer, λmax in the photoluminescence spectrum of these films changed to 365nm, which means that the conjugation of these PAHPV films was completed.