Vegetation has a great importance in erosion control and slope stabilization, protecting and restraining the surface soil and increasing the strength and competence of the soil mass. However, normal green soil have poor adhesion to slopes. In order to enhance the adhesion, therefore, the vegetation effect of green slope soil mixed with cement materials was investigated in this study.

Environmental pollution is the major problem associated with rapid industrialization, urbanization and rise in living standards of people. In order to reduce environmental pollution, therefore, shielding materials using industrial waste resources were developed and the radiation shielding performance was evaluated.

In order to solve the problem of natural aggregate exhaustion, several types of industrial waste have been studied for recycling of construction materials. In general, steel slag has been used as aggregate in concrete, however, steel slag has a problem of causing volume expansion by F-CaO. Therefore, in this study, the expansion properties are compared with aging period to solve the problem of the steel slag expansion. According to the test results, the expansion of the steel slag decreased regardless of the types of steel slag during aging period. And, the Electronic Arc Furnace Oxidizing Slag(EAF) had the better reduction in expanding than the Converter Slag(CS).

Recently, the industrial waste resources have been continually developed because of a lack of natural aggregate. In this study, before the applicability of concrete using steel slag as aggregate, the properties were evaluated. From the test results, it is showed that the water aging period of the steel slag had no effect on the air contents, slump, compressive strength and density.

In this study, we investigated the possibility of using the cementitious material as a base material for rock vegetation through the measurement of adhesion force, internal friction angle and vegetation observation of green soil. From the results, The adhesion force, internal friction angle measurements and the final growth state were improved than that of the existing green soil, so that it could be effectively applied to rock slope.

Filler material (concrete or mortar) has been used for shielding radioactive waste, however, it is proceeded out evaluation for radiation shielding performance. So, it is needed to check the property in the shielding performance. Therefore, in this paper, mechanical properties of concrete was evaluated for the applicability using heavyweight waste glass as fine aggregate of filler material. From the test results, compressive and elasticity modulus were significantly affected by substitution of heavyweight waste glass, however, it could be improved the performance by using mineral admixture as binder.

전자폐기물의 발생량이 급증하고 있고, 전자폐기물로 인한 환경오염 혹은 자원낭비등과 같은 문제를 야기하고 있다. 따라서 전자폐기물 안에 포함된 중금속을 재활용할 수 있는 기술 개발이 필요하다. 한편, 채움재(콘크리트 혹은 모르타르)는 방사성폐기물의 차폐를 위해 사용되나, 방사성 차폐 성능을 확보한 재료를 적용하고 있지 않다. 따라서 채움재는 차폐성능에 관한 신뢰가 부족한 상황이다. 그러므로 본 연구에서는, 전자폐기물을 채움재의 잔골재로 적용하기 위하여 콘크리트의 역학적 특성을 평가하였다. 실험결과, 압축강도, 휨강도, 탄성계수 및 1μm 영역의 공극이 상당히 영향을 받는 것으로 나타났으나, 광물질 혼화재를 결합재로 사용하면 성능이 개선되었다. 따라서 전자폐기물은 채움재의 잔골재로써 적용이 가능할 것으로 판단된다.

Electrical waste, such as heavy weight waste glass, has become a global concern in terms of resource recycling. At the same time, aggregate is one of the most widely used infrastructure materials, and it is being exhausted. So, in this paper, the heavy weight waste glass is considered as aggregate due to its physical characteristics and chemical composition. From the results, when the heavy weight waste glass substitution ratio increase, the compressive strength and flexural strength decreased.

In this paper, the slope adhesion force of the developed green slope soil was evaluated by simulating rainfall intensity. From the results, the slope failure didn't occur at all conditions. As the slope angle increases, however, the damage decreased. The developed green slope soil is considered to have sufficient adhesion capacity to the slope.

In this paper, the flexural test of concrete member damaged due to Calcium leaching were performed to evaluate the characteristics of structural behavior. From the results, yield load, maximum load and flexural rigidity of RC member damaged by calcium leaching were decreased and the depth of the neutral axis was increased.

In this paper, the moisture content of fertilizer on properties of green slope soil using mineral additives are evaluated. From the results, when the moisture content of fertilizer increases, the soil hardness (penetrometer cone index) is decreased. And the moisture content of fertilizer increases, the shrinkage decrease at early ages, however, shrinkage increased with the ages.

In this paper, the moisture content of fertilizer on properties of green slope soil using mineral additives are evaluated. From the results, when the moisture content of fertilizer increases, the soil hardness (penetrometer cone index) is decreased. And the moisture content of fertilizer increases, the shrinkage decrease at early ages, however, shrinkage increased with the ages.

In this paper, the material characteristics of field applied green slope soil for development of vegetation shotcrete using mineral additive are evaluated. From the results, after a consolidation of certain level is proceeded, soil hardness and soil strength are not affected by ages. However, in order to ensure slope stability, the cohesion should be improved of green slope soil.

In the current concrete structure of the highway is still the major problem most of concrete deterioration caused by the freeze-thaw and deicing salt, which is of issues that are not completely resolved. In particular, a single freezing event does not cause much harm, durability of concrete under multi-deterioration environment by repeated freeze-thaw and deicing salt is rapidly degraded and reduce its service life. In this study, the exposure environmental condition according the regional highway points were established. The damage condition and chloride content of the concrete at general and severe environmental exposure condition were also investigated. In addition, the experimental test of chloride ion permeability, scaling resistant and freeze-thaw resistance were carried out to improve the durability of the mechanical placing concrete of subsidiary structure. According to the results of this study, in observation of concrete surface condition, the concrete exposed by severe environmental condition showed broad ranges of damage with high chloride contents. Meanwhile, the water-binder(W/B) ratio and the less water content, and fly ash concrete than the specified existing mix proportion is significantly improved the durability. Also, the optimal mix proportion derived for test is satisfied the strength and air contents, water-binder ratio, and durability criteria of concrete specifications, as well as service life seems greatly improved.

The objective of this study is the development of an artificial soil composition for vegetation in rock slope condition. In this study, the suitability of artificial soils added the cement-based materials is considered. The results show that the pH value of artificial soil added the micro cement was kept in the range of 7.86 to 8.00.

In this paper, the material characteristics of green slope soil for application to vegetation shotcrete using mineral additive are evaluated. From the results, when the compaction level increase, soil hardness and soil strength are increased. However, the cohesion and angle of internal friction are not significantly affected by mix proportions.

In this study, chloride penetration of calcium leached concrete according to mineral admixture ratio were compared with OPC. From the results, it showed that chloride diffusion coefficient in calcium leached concrete were increased as calcium leaching period increase. However, the chloride diffusion coefficient of BFS case showed the better resistance than Fly Ash case. And, the distribution of chloride diffusion coefficient was significantly changed by calcium leaching period.

In this study, the process for the cause of lateral movement of bridges is suggested. Based on the monitoring of shoe and pier movement, the lateral movement of birdges is studied. As a result, the process is applicable for the small lateral movement of the bridges.

다양한 열화 인자에 의해 저감된 콘크리트의 내구성은 구조물의 구조적 성능과 사용 수명에 부정적인 영향을 미치게 되며 콘크리트 연구 분야 중에서도 매우 중요하고 매력적인 주제라고 할 수 있다. 이러한 이유로 콘크리트의 내구성과 관련된 많은 연구들이 발표되었으나 물리-화학적 열화에 기인하는 콘크리트의 본질적인 물성 변화에 주된 초점이 맞춰져 왔으며, 콘크리트 내구성과 구조물의 구조적 성능 사이의 관계 정립은 아직 미흡한 실정이다. 본 연구에서는 콘크리트의 강도 감소에 원인이 되는 칼슘 용출 열화를 적용하였으며, 열화 정도에 따른 구조적 거동을 평가하기 위하여 열화 손상을 입은 콘크리트 부재의 압축 및 휨 거동 실험을 수행하고 그 결과를 비선형 유한요소해석 결과와 비교 분석하였다. 연구 결과에 따르면 칼슘 용출 열화는 콘크리트의 압축 강도를 저하시키며, 열화가 진행됨에 따라 취성 거동에서 연성 거동으로 변화되는 경향을 나타냈다. 또한 열화에 의한 압축 영역의 손상 정도가 심화될수록 RC 부재의 내하력과 강성은 저하되었으며, 이러한 구조적 거동은 ABAQUS의 CDP 모델을 사용한 비선형 유한요소해석의 결과와도 비교적 잘 일치하였다.

In this study, the rahmen bridge damaged by the chloride attack was investigated. According to the investigation, the degraded concretes on cantilever kerb and end part were intensively observed. Thus, the chloride content test and half-cell method were performed to evaluate the degraded parts. As a result, the contents of chloride on degraded parts were C and D grade. On the other hand, the half-cell potential values of rebar in degraded concrete were measured with the minor corrosion. Thus, the freeze-thawing action due to deicing water is more influential than the expansion of rebar corrosion by chloride attack. Consequently, the economical repairs of degraded parts is more favorable than the replacement of the degraded parts. Also, it is necessary to inhibit the corrosion of rebar in concrete.