This research investigated how adding Sb (0.75, 1.0, 2.0 and 5.0 wt%) to as-extruded aluminum alloys affected their microstructure, mechanical properties, electric and thermal conductivity. The addition of Sb resulted in the formation of AlSb intermetallic compounds. It was observed that intermetallic compounds in the alloys were distributed homogenously in the Al matrix. As the content of Sb increased, the area fraction of intermetallic compounds increased. It can be clearly seen that the intermetallic compounds were crushed into fine particles and homogenously arrayed during the extrusion process. As the Sb content increased, the average grain size decreased remarkably from 282.6 μm (0.75 wt%) to 109.2 μm (5.0 wt%) due to dynamic recrystallization by the dispersed intermetallic compounds in the aluminum matrix during the hot extrusion. As the Sb content increased from 0.75 to 2.0 wt%, the electrical conductivity decreased from 61.0 to 59.8 % of the International Annealed Copper Standard. Also, as the Sb content increased from 0.75 to 2.0 wt%, the ultimate tensile strength did not significantly change, from 67.3 to 67.8 MPa.

This research investigated the effect of Si addition on the microstructure, mechanical properties, electric and thermal conductivity of as-extruded Al 6013 alloys. As the content of Si increased, the area fraction of the second phase increased. As the Si content increased, the average grain size decreased remarkably, from 182 (no Si addition) to 142 (1.5Si), 78 (3.0Si) and 77 μm (4.5Si) due to dynamic recrystallization by the dispersed second particles in the aluminum matrix during the hot extrusion. As the Si content increased, the yield strength and ultimate tensile strength increased. The maximum values of yield strength and ultimate tensile strength were 224 MPa and 103 MPa for the 6013-4.5Si alloy. As the amount of Si added increased, the electrical and thermal conductivity decreased. The electrical and thermal conductivity of the Al6013-4.5Si alloy were 44.0% IACS and 165.0 W/mK, respectively. The addition of Si to Al 6013 alloy had a significant effect on its thermal conductivity and mechanical properties.