PURPOSES : There has been increasing interest in South Korea on warm-mix asphalt (WMA) and cold-mix asphalt (CMA) technologies that allow production of asphalt pavement mixtures at comparatively lower temperatures than those of hot-mix asphalt (HMA) for use in pavement engineering. This study aims to evaluate the feasibility of replacing HMA pavement with WMA pavement with the goal of reducing CO2 emissions associated with asphalt production for road construction. METHODS : Changes in the dynamic modulus characteristics of WMA and HMA according to short-term and long-term aging were evaluated. In addition, the effects of water damage were evaluated for short- and long-term aging stages. RESULTS : For WMA, in the process of mixing and short-term aging, early-age dynamic modulus decreased owing to low temperature and reduced short-term aging (STA) time. This could result in early damage to the asphalt pavement depending on the applied traffic load and environmental load. CONCLUSIONS : Mastercurves of the dynamic modulus were used for comparative analysis of WMA and HMA. Compared to the dynamic modulus after STA of HMA, the estimated aging time determined by experiments for WMA to achieve the required stiffness was more than 48 hours, which is equiva-lent to approximately 4 to 5 years real service life when converted. It is considered that further studies are needed for performance optimization to achieve early-age performance of the asphalt mixes.

PURPOSES: This study evaluated the effect of fog seal treatment utilizing an agricultural oil-based asphalt concrete sealant (ABCS) on the long-term performance of an asphalt pavement. METHODS: Fog seal treatment using ABCS was applied on 800 m of the pavement section in the test section with a total length of 2,400 m; the remaining pavement section was not considered for this treatment. A series of laboratory and field tests were conducted on both sections, including a Marshall stability test, penetration test, viscosity test, skid resistance test, and pavement surface macrotexture test. In addition, the pavement condition index (PCI) was determined 8 years after the ABCS application to evaluate the effect of the ABCS treatment on the pavement’s long-term performance. RESULTS : The ABCS-treated section exhibited a PCI of 75, whereas the non-treated section exhibited a value of 64. Furthermore, a MicroPAVERTM‚ pavement management system determined that the pavement deterioration rates (i.e., drops in PCI) were 3.6 and 5.1 per year for the ABCS-treated and non-treated sections, respectively. CONCLUSIONS : The results of the series of laboratory and field tests revealed that the ABCS treatment increased the pavement performance life by approximately 3.5 years.