PURPOSES : There has been increasing interest in South Korea on warm-mix asphalt (WMA) and cold-mix asphalt (CMA) technologies that allow production of asphalt pavement mixtures at comparatively lower temperatures than those of hot-mix asphalt (HMA) for use in pavement engineering. This study aims to evaluate the feasibility of replacing HMA pavement with WMA pavement with the goal of reducing CO2 emissions associated with asphalt production for road construction. METHODS : Changes in the dynamic modulus characteristics of WMA and HMA according to short-term and long-term aging were evaluated. In addition, the effects of water damage were evaluated for short- and long-term aging stages. RESULTS : For WMA, in the process of mixing and short-term aging, early-age dynamic modulus decreased owing to low temperature and reduced short-term aging (STA) time. This could result in early damage to the asphalt pavement depending on the applied traffic load and environmental load. CONCLUSIONS : Mastercurves of the dynamic modulus were used for comparative analysis of WMA and HMA. Compared to the dynamic modulus after STA of HMA, the estimated aging time determined by experiments for WMA to achieve the required stiffness was more than 48 hours, which is equiva-lent to approximately 4 to 5 years real service life when converted. It is considered that further studies are needed for performance optimization to achieve early-age performance of the asphalt mixes.

PURPOSES:The objectives of this study are to evaluate moisture sensitivity of various asphalt mixtures and to suggest an alternate method for the dynamic immersion test, which is used to determine the application of anti-stripping agent, by analyzing bond strength.METHODS:The bond strength of various asphalt mixtures such as hot mix asphalt, warm mix asphalt, and polymer-modified asphalt was evaluated by the ABS test. In order to characterize moisture sensitivity at different temperatures of the mixtures, the ABS test was conducted at -10°C, 5°C, 20°C, 40°C, and 54°C under both dry and wet conditions. The concept of the bond strength ratio was applied for objective moisture sensitivity analysis. Moreover, the bond strength characteristic was compared to the dynamic immersion test to suggest an alternate method to determine the application of anti-stripping agent.RESULTS AND CONCLUSIONS :Overall, the polymer-modified asphalt demonstrates the highest bond strength characteristic regardless of moisture condition and temperature. The bond strength characteristic displays a highly reliable linear relationship from 5°C to 40°C, and the relationship could be used to predict bond strength at any intermediate temperature. Based on the analysis of bond strength and retained asphalt ratio, the bond strength value of 1254 kPa could be applied as a criterion for anti-stripping agent.