Metal powder for dust core application was developed. The powder can be produced improved high-pressure water atomization process. The process has produced powder of spherical shape and lower coercivity. The dust core obta ined shows lower core loss.

The MIM industry is currently focusing on parts that are used in automobiles and medical instruments. Many of the parts in these categories are very small and often not easy to machine because of its complex geometry. Therefore MIM is well suited for the production of these parts. We tested the sinterability of SUS316L ultra fine powders (3,4, 6, 8micron) produced by ATMIX high-pressure water-atomization, and it showed excellent results. A density of 97% theoretical was obtained by sintering at 1373K when using the ultra fine powder (3micron). Specifically, the finer the powder size, higher was the sintered density. The surface roughness and accuracy are also greatly improved with ATMIX ultra fine powder.

Granulated powders, prepared from PF-5F(D50=4μm), PF-10F(D50=6μm) and PF-20F(D50=10μm) water atomized powder, were compacted, debound and sintered to evaluate the properties of sintered parts. As a result, the relative sintered density of about 97% at sintering temperature of 1423K was obtained. It can be considered that by using granulated finer particle size powder, mechanical properties of sintered parts were also improved.