Graphene fiber is considered as a potential material for wearable applications owing to its lightness, flexibility, and high electrical conductivity. After the graphene oxide (GO) solution in the liquid crystal state is assembled into GO fiber through wet spinning, the reduced graphene oxide (rGO) fiber is obtained through a reduction process. In order to further improve the electrical conductivity, herein, we report N, P, and S doped rGO fibers through a facile vacuum diffusion process. The precursors of heteroatoms such as melamine, red phosphorus, and sulfur powders were used through a vacuum diffusion process. The resulting N, P, and S doped rGO fibers with atomic% of 6.52, 4.43 and 2.06% achieved the higher electrical conductivities compared to that of rGO fiber while preserving the fibrious morphology. In particular, N doped rGO fiber achieved the highest conductivity of 1.11 × 104 S m−1, which is 2.44 times greater than that of pristine rGO fiber. The heteroatom doping of rGO fiber through a vacuum diffusion process is facile to improve the electrical conductivity while maintaining the original structure.

배초향은 항동맥경화나 항박테리아의 특성을 가지는 한약재에 널리 사용되는 영년생 약용식물이다. 연구의 목적은 수경재배에서 배양액의 종류와 PPFD값에 따른 배초향의 생장 및 항산화 물질의 변화를 조사하는 것이다. 배초향은 주야간 16:8 시간의 일장조건에서 150과 200 μmol·m-2·s-1 PPFD 조건과 일본원시(HES), 서울시립대(UOS), 유럽채소연구소(EVR), 오오츠카 배양액(OTS)을 이용하여 6주간 재배하였다. OTS 배양액조 건에서 자란 배초향의 지상부 및 지하부 건물중은 다른 배양액 처리구와 비교하여 유의적으로 높았다. 배초향의 틸리아닌 함량은 OTS 처리에서 가장 높았으며 다음으로 EVR, HES, UOS 순서로 낮아졌다. 총 아카세틴의 함량은 EVR처리에서 가장 높았으나 OTS처리와는 유의적 차이를 보이지 않았다. 또한 200 μmol·m-2·s-1 PPFD 조건에서 자란 배초향은 PPFD 150처리구와 비교하여 유의적으로 생체중과 건물중이 증가하였으며 기능성 물질은 틸리아닌과 아카세틴의 함량도 높았다. 본 연구는 수경재배 방식을 이용하여 식물공장에서 배초향을 재배할 경우 200 μmol·m-2·s-1 PPFD 조건과 OTS 배양액 조건에서 경제적인 광원조건으로 최적 바이오매스 생산량과 틸라아닌과 아카세틴의 함량을 증가시킬 수 있을 것으로 제안한다.