PURPOSES: The objective of this study is to investigate the properties of recycled asphalt binders with five different rejuvenators, in order to evaluate the applicability of the recycled asphalt binders compared with the original asphalt binder. METHODS: In order to simulate recycled asphalt binders, fresh asphalt binders are aged by various Superpave aging procedures, such as the rolling thin-film oven (RTFO) and the pressure aging vessel (PAV). Then, selected rejuvenators are added to the aged asphalt binders in the amount of 5%, 10%, and 15%. The asphalt binder properties are evaluated by the dynamic shear rheometer (DSR), the rotational viscometer (RV), and the bending beam rheometer (BBR). In this study, AP-5 (penetration grade 60-80, PG 64-16) asphalt binder is used. A total of five types of rejuvenators are employed. RESULTS AND CONCLUSIONS : When considering aged asphalt without a new asphalt binder, it seems that the percentage of rejuvenator used in Korea is a bit too low, and that it fails to possess the characteristics of the original binder. From the current practice of evaluating the properties of recycled binder based on penetration ratio only, the amount of rejuvenator required is similar for the long-term-aged binder, but is excessive for the longest-term aged binder, causing deterioration of workability and stiffness of the recycled binder.

PURPOSES: The objectives of this study were to develop a new polymer-modified emulsion for application to tack coats and to evaluate its properties by comparing it with other types of asphalt emulsions, with the goal of providing an enhanced tack coat material for use in construction. METHODS: Modified asphalt binders were developed from using SBS and SBR latex in the laboratory, and their fundamental properties, such as their penetration index and PG grade, were evaluated. Based on the properties, a new tack coat material was developed. To evaluate the newly developed asphalt emulsion, the bonding strength between the two layers of HMA was measured by applying a uniaxial tensile test and shear test. For the tests, a total of four different conditions were applied to the specimens, including the developed asphalt emulsion, latex modified asphalt emulsion, conventional asphalt emulsion, and non-tack coating. RESULTSAND CONCLUSIONS: Overall, the developed asphalt emulsion exhibits the best bonding strength behavior among all of the three types. Also, the two types of polymer-modified emulsions were found to be better for application for use as a tack coat than a conventional emulsion. Especially, at a high temperature (50℃), the conventional asphalt emulsion no longer acts as a tack coating material. Therefore, the polymer-modified emulsion should be considered for application to tack coat construction during the summer.

PURPOSES: The objective of this study is to compare the densities of asphalt pavements measured both in the field and in the laboratory, and also to evaluate the applicability of field density measuring equipment, such as the pavement quality indicator (PQI), by using statistical analysis. METHODS: For the statistical analysis of the density measured from asphalt pavement, student t-tests and a coefficient of correlation are investigated. In order to compare the measured densities, two test sections are prepared, with a base layer and an intermediate layer constructed. Each test section consists of 9 smaller sections. During construction, the field densities are measured for both layers (base and intermediate) in each section. Core samples are extracted from similar regions in each section, and moved to the laboratory for density measurements. All the measured densities from both the field and laboratory observations are analyzed using the selected statistical analysis methods. RESULTS AND CONCLUSION : Based on an analysis of measured densities, analysis using a correlation coefficient is found to be more accurate than analysis using a student t-test. The correlation coefficient (R) between the field density and the core density is found to be very low with a confidence interval less than 0.5. This may be the result of inappropriate calibration of the measuring equipment. Additionally, the correlation coefficient for the base layer is higher than for the intermediate layer. Finally, we observe that prior to using the density measuring equipment in the field, a calibration process should be performed to ensure the reliability of measured field densities..

PURPOSES : The objective of this study is to develop new pothole repair materials using polyurethane-modified asphalt binder, and to evaluate them relative to current pothole repair materials in order to improve the performance of repaired asphalt pavement. METHODS : In the laboratory, polyurethane-modified asphalt binder is developed, and then asphalt binder is added to produce pothole repair materials. In order to evaluate the properties of this new pothole repair material, both an indirect tension strength test and a direct tension strength test are performed to measure the material strength and bond strength, respectively. Additionally, the basic material properties are evaluated using the asphalt cold mix manual. The strength characteristics based on curing times are evaluated using a total of 7 types of materials (3 types of current materials, 2 types of new materials, and 2 types of moisture conditioned new materials). The indirect tension strength tests are conducted at 1, 2, 4, 8, 16, and 32 days of curing time. The bond strength between current HMA(Hot Mix Asphalt) and the new materials is evaluated by the direct tension strength test. RESULTS AND CONCLUSIONS : Overall, the new materials show better properties than current materials. Based on the test results, the new materials demonstrate less susceptibility to moisture, faster curing times, and an improved bond strength between HMA and the new materials. Therefore, the use of the new materials reported in this study may lead to enhanced performance of repairs made to asphalt pavement potholes.

PURPOSES : Compared to the criteria from advanced countries, Korea has conservative criteria for the buried depth of pipeline (about 30~70cm deeper) causing the waste of cost and time. Therefore, this research investigated the effect of various buried depths of pipeline on pavement performance in order to modify the criteria to be safe but economical. In addition, a recycled aggregate which is effective in economical and environmental aspect was evaluated to be used as a refilling material. METHODS : In this study, total 10 pilot sections which are composed with various combinations of pavement structure, buried depth of pipeline, and refilling material were constructed and the telecom cable was utilized as a buried pipeline. During construction, LFWD (Light Falling Weight Deflectometer) tests were conducted on each layer to measure the structural capacity of underlying layers. After the construction is completed, FWD (Falling Weight Deflectometer) tests and moving load tests were performed on top of the asphalt pavement surface. RESULTS : It was found from the LFWD and FWD test results that as the buried depth decrease, the deflections in subbase and surface layer were increased by 30% and 5~10%, respectively, but the deflection in base layer remained the same. In the moving load test, the longitudinal maximum strain was increased by 30% for 120mm of buried depth case and 5% for 100mm of buried depth case. Regarding the effect of refilling material, it was observed that the deflections in subbase and surface layer were 10% lager in recycled aggregate compared to the sand material. CONCLUSIONS : Based on the testing results, it was found that the change in buried depth and refiliing material would not significantly affect the pavement performance. However, it is noted that the final conclusion should be made based on an intensive structural analysis for the pavement under realistic conditions (i.e., repeated loading and environmental loading) along with the field test results.

The purpose of this study is to find out the relationship between overburden load and lateral stiffness of new traditional Korean-style house. The experiment was carried out with the 1/4 scale model under displacement control static loading. As the overburden load increased, the lateral stiffness of the new traditional Korean-style house also increased

In this study, we developed section list table for horizontally overlapped structural members of new traditional Korean-style houses. Wood grade, roof load, member length etc were considered as design variables. We expect that the developed section list table can help architectural designer of new traditional Korean-style house in their early design stage

In this study, we suggest the process that can effectively evaluate safety and serviceability of purlin members of new traditional Korean-style house. It is composed of three parts, that is, input, structurecalculation, and structure-evaluation part. We expect that this suggested process can help structural engineers to secure safety and serviceability of new traditional Korean-style house.

Generally deformation of wooden structures is larger than that of concrete and steel structures. We measured deformation of traditional Korean-style houses periodically and analyzed their deformation patterns. We expect that this study can help to reveal causes of long-term deformation of traditional Korean-style houses.