        1.
        2012.03 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        In this work, AlON-Al2O3 coatings were prepared on Al2021 alloy by the electrolytic plasma processing (EPP) method. The experimental electrolytes include: 2 g/l NaOH as the electrolytic conductive agent, 10 g/l Na2AlO2 as the alumina formative agent, and 0.5 g/l NaNO2, NaNO3, and NH4NO3 as the nitride inducing agents. The effects of different nitrogen inducing agents were studied by a combined compositional and structural analyses of the ceramic coatings carried out by Xray diffractometry (XRD) and scanning electron microscopy (SEM) for the specimens EPP-treated at room temperature for 15 min under a hybrid voltage of 260 DC along with an AC 50 Hz power supply (200 V). Microhardness tests and wear tests were carried out to correlate the evolution of the microstructure and the resulting mechanical properties. Potentiodynamic polarizations and immersion corrosion tests were carried out in 3.5wt% NaCl water solutions under static conditions in order to evaluate the corrosion behavior of the coated samples. The results demonstrate that NaNO2 is proven to be a good nitrogen inducing agent to produce high quality AlON-Al2O3 ceramic coatings.
        3,000원
        2.
        2011.04 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        Perovskite manganites such as RE1-xAxMnO3 (RE = rare earth, A = Ca, Sr, Ba) have been the subject of intense research in the last few years, ever since the discovery that these systems demonstrate colossal magnetoresistance (CMR). The CMR is usually explained with the double-exchange (DE) mechanism, and CMR materials have potential applications for magnetic switching, recording devices, and more. However, the intrinsic CMR effect is usually found under the conditions of a magnetic field of several Teslas and a narrow temperature range near the Curie temperature (Tc). This magnetic field and temperature range make practical applications impossible. Recently, another type of MR, called the low-field magnetoresistance(LFMR), has also been a research focus. This MR is typically found in polycrystalline half-metallic ferromagnets, and is associated with the spin-dependent charge transport across grain boundaries. Composites with compositions La0.7(Ca1-xSrx)0.3MnO3)]0.99/(BaTiO3)0.01 [(LCSMO)0.99/(BTO)0.01]were prepared with different Sr doping levels x by a standard ceramic technique, and their electrical transport and magnetoresistance (MR) properties were investigated. The structure and morphology of the composites were studied by X-ray diffraction (XRD) and scanning electronic microscopy (SEM). BTO peaks could not be found in the XRD pattern because the amount of BTO in the composites was too small. As the content of x decreased, the crystal structure changed from orthorhombic to rhombohedral. This change can be explained by the fact that the crystal structure of pure LCMO is orthorhombic and the crystal structure of pure LSMO is rhombohedral. The SEM results indicate that LCSMO and BTO coexist in the composites and BTO mostly segregates at the grain boundaries of LCSMO, which are in accordance with the results of the magnetic measurements. The resistivity of all the composites was measured in the range of 90-400K at 0T, 0.5T magnetic field. The result indicates that the MR of the composites increases systematically as the Ca concentration increases, although the transition temperature Tc shifts to a lower range.
        3,000원
        3.
        2010.03 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        The (1-x)La0.7Sr0.3MnO3(LSMO)/xZnFe2O4(ZFO) (x = 0, 0.01, 0.03, 0.06 and 0.09) composites were prepared by a conventional solid-state reaction method. We investigated the structural properties, magnetic properties and electrical transport properties of (1-x)LSMO/xZFO composites using X-ray diffraction (XRD), scanning electron microscopy (SEM), field-cooled dc magnetization and magnetoresistance (MR) measurements. The XRD and SEM results indicate that LSMO and ZFO coexist in the composites and the ZFO mostly segregates at the grain boundaries of LSMO, which agreed well with the results of the magnetic measurements. The resistivity of the samples increased by the increase of the ZFO doping level. A clear metal-to-insulator (M-I) transition was observed at 360K in pure LSMO. The introduction of ZFO further downshifted the transition temperature (350K-160K) while the transition disappeared in the sample (x = 0.09) and it presented insulating/semiconducting behavior in the measured temperature range (100K to 400K). The MR was measured in the presence of the 10kOe field. Compared with pure LSMO, the enhancement of low-field magnetoresistance (LFMR) was observed in the composites. It was clearly observed that the magnetoresistance effect of x = 0.03 was enhanced at room temperature range. These phenomena can be explained using the double-exchange (DE) mechanism, the grain boundary effect and the intrinsic transport properties together.
        4,000원