Cu/PET composite films are widely used in a variety of wearable electronics. Lifetime of the electronics is determined by adhesion between the Cu film and the PET substrate. The formation of an anisotropic nanostructure on the PET surface by surface modification can enhance Cu/PET interfacial adhesion. The shape and size of the anisotropic nanostructures of the PET surface can be controlled by varying the surface modification conditions. In this work, the effect of Cu/PET interface nanostructures on the failure mechanism of a Cu/PET flexible composite film is studied. From observation of the morphologies of the anisotropic nanostructures on plasma-treated PET surfaces, and cross-sections and surfaces of the fractured specimens, the Cu/PET interface area and nanostructure width are analyzed and the failure mechanism of the Cu/PET film is investigated. It is found that the failure mechanism of the Cu/PET flexible composite film depends on the shape and size of the plasmatreated PET surface nanostructures. Cu/PET interface nanostructures with maximal peel strength exhibit multiple craze-crack propagation behavior, while smaller or larger interface nanostructures exhibit single-path craze-crack propagation behavior.

Oxalic acid has a nematicidal activity against the root-knot nematode Meloidogyne incognita. High producer of oxalic acid was isolated, and then named as Aspergillus niger F22. Oxalic acid production was investigated under various temperatures from 20 – 33oC and rotational speeds in 5 L jar fermenters. Yield of oxalic acid increased with decreasing temperature. The highest yield was obtained at 23oC, showing the yield of oxalic acid of 8.7 g/L, whereas oxalic acid production was least at 33oC. At 20oC, the yield was lower than that of 23oC. At a rotational speed of 300 rpm, serious oxygen depletion was present from 48 - 72 h, resulting in low productivity of 26.2 mg /L·h. When a rotational speed was set at 600 rpm, dissolved oxygen tension was over 40% and oxalic acid production increased up to approximately 55%. Viscosity during the culture differed with temperatures. Viscosity increased with the increment of temperatures. When A. niger F22 was cultured at 23oC, viscosity was 810 cP, which was favorable for oxalic acid production.

This study was carried out to estimate odors emitted from toilets in Mugunghwa trains. Two parameters, odor intensity and odor concentration, were used for odor estimation. A direct olfactory method to observe odor intensity for 67 toilets and an air dilution olfactory method to estimate odor concentration for 6 samples were performed. Results showed that odor concentrations in toilets in trains ranged from 6 OU/m3 to 30 OU/m3, and odor intensity in 67 toilets varied from 0 degree to 3.3 degree. The results suggest that odors emitted from existing toilets should be controlled because the odor intensity in 16 toilets reached a level that resulted in complaints about the odor.

황화수소 등 유황계 악취물질은 매우 낮은 최소감지농도를 갖고 있기 때문에 악취를 제거하기 위해서는 출구에서 악취가 검출되지 않는 적정 부하량에 대해 검토가 이루어져야 한다. 본 연구에서는 활성탄을 가공하여 제작한 습윤 상태의 활성탄소섬유를 이용하여 현장조건과 유사하게 황화합물악취 H2S 10 ppm, MT 3 ppm, DMS 1.5 ppm 3성분의 혼합가스에 대해 약 130일 동안 제거실험을 수행하였다. 그 결과, H2S는 유입부하량을 0.78 g-H2S / kg ACF·d 이하로 설정하여 운전하는 것이 필요하며, MT는 불완전산화 부산물인 DMDS가 출구에서 검출되어 악취를 유발하므로 안정적인 운전을 위해서는 유입부하량을 0.27 g-MT / kg ACF·d 이하로 설정하여 운전하는 것이 필요한 것으로 나타났다. DMS는 유입부하량의 변화에 관계없이 거의 제거되지 않는 것으로 나타났다.

본 연구는 양성전해질막의 금속이온 특성을 조사하기 위하여 Taurine (TAU)막을 제조하였다. 제조방법으로는 방사선조사법에 의한 Glycidyl methacrylate (GMA)의 중공사막 표면위에 고정시키고, 이후 Taurine의 염기성 부분인 -NH2기(amine fuction)와 GMA의 glycididyl의 개환 반응을 통하여 안정된 막을 형성하도록 하였다. 한편 TAU막과 비교를 위해 GMA가 고정된 중공사 막에 Sodium sulfite로 화학적 결합을 형성 SS막을 제조하였다. 이렇게 제조된 TAU막의 타우린 밀도가 높아져도 투과유속은 0.9 m/h로 변화 없으나, SS막은 술폰산기의 밀도가 높아짐에 따라 투과유속이 급격히 감소하는 것을 나타내었다. 타우린 밀도가 0.8 mmol/g인 막을 사용한 결과 금속이온의 량은 Cu > Cd > Mg > Sb > Pb의 순으로 나타내었다. 전반적으로 타우린막은 전화율과 밀도의 증가에 따라 많은 양의 금속이온 흡착과 높은 투과유속을 나타내었다.

본 연구의 목적은 중금속 흡착을 위한 방사선 그라프트 중합법에 의한 이온교환막의 성능 향상을 위한 것이다. 그라프트 체인의 이온교환기에 의해 체인이 막의 pore를 방해하여 투과유속이 크게 저하되는 문제를 해결하고자 그라프트 체인과 체인사이를 N-ethyleneglycoldimethacrylate계 가교제를 첨가하여 투과유속이 저하되는 문제를 해결하고자 했다. 이때 사용된 가교제는 길이가 서로 다른 ethylene glycol dimethacrylate (EDMA)와 diethylene glycol dimethacrylate (DDMA)를 사용하였다. GMA 막에 가교제가 첨가된 이온교환막에 술폰산기를 첨가한 막을 이용하여 중금속 이온(Pb2+) 흡착을 하였다. 술폰산기 밀도가 1.40 mmol/g인 EDMA막은 13.82 mg/g을 흡착하였고, 술폰산기 밀도가 2.14 mmol/g인 DDMA막은 17.37 mg/g의 흡착량을 보였다.

최근 다엽콜리메이터를 부착한 선형가속기를 이용한 방사선수술의 빈도가 점차 높아지고 있다. 이러한 정교한 방사선 수술은 소조사면 내에 고선량의 방사선이 집중적으로 조사되기 때문에 체계적이고 정확한 정도관리가 필수적이다. 본 연구는 PIB(Particle in Binder) 방식 중 침전법을 이용하여 400 ㎛ 두께의 요오드화납(PbI2)과 요오드화수은(HgI2) 광도전체 센서 시편를 제작하였다. 제작된 시편의 전기적 특성은 암전류, 출력전류, 응답특성 및 선형성을 평가하였다. 평가 결과, HgI2 가 우수한 신호발생량과 선형성을 보였다. 끝으로, 두께에 따른 HgI2 센서의 신호반응 특성 결과, 400 ㎛ 두께에서 신호발생효율이 가장 높았고, ±2.5 % 이내의 우수한 재현성을 보였다.