The properties of dust collected from electric arc furnace of ferro manganese production units was investigated, and also the metallic manganese was recovered from the dust by aluminothermy process. The ferromanganese dust collected from electric arc furnace contained about 15% of manganese oxide (Mn3O4) and 9% of carbon as the contaminant, and have a 5um of 50% median diameter and irregular particle shape. The carbon contaminant in the dust could be reduced until about 0.1~0.5% level by roasting in the air at a temperature of 600~900C for 60minutes. The recovery of manganese could not be carried out using only ferromanganese dust from electric arc furnace by aluminothermy process, but the ferromanganese which contained manganese of about 92% and iron of about 5% could be obtained from the mixture of ferromanganese dusts from electric arc furnace and converter. The best mixing condition of dust fixed at electric arc furnace dust / converter dust ratio of 1:9 and 2:8, and the mixing rato of 3:7 or more could not separated the metal and slag from the reactant after aluminothermy reaction.

Indoor air quality including metro subway is of recent interests in large cities. Inflow air to the inside of the train and circulating air flow through MVAC of stations contain large amount of iron based fine particles. This paper evaluated the collection of such a dust by magnetic filters as comparing to conventional particle capturing mechanisms such as inertia, direct impaction and diffusion. It was found that filtration velocity, magnetic field intensity, and fiber size were the most important parameters for magnetic filtration. Application of magnetic force obviously enhances the collection efficiency particularly in fine modes smaller than 10 mm. However, its effect was found greater in 2.5 mm than submicron particles.