이방성과 등방성을 갖는 두 종류의 피치계 탄소섬유를 TGA장치를 이용하여 CO2gas와 공기중에서 등온산화반응을 실시하였다. CO2 gas보다 공기중에서의 산화가 훨씬 빠르게 일어났으며, 600˚C공기중에서 등방성 T-10IS섬유는 이방성 HM-60섬유보다 23.9배나 빠른 산화속도를 보였다. 실험적으로 구한 활성화에너지를 저온에서 36-56Kcal/mole의 값을 가지며, 고온에서는 6-13Kcal/mole의 값을 나타내었다. 반응기구(zone 1,2,3)의 천이도는 T-10IS섬유보다 HM-60 섬유가 높았으며, 공기중에서보다 CO2 gas분위기에서 더 높게 나타났다. SEM으로 관찰된 표면상변화로부터 탄소섬유의 산화반응은 섬유의 결함을 따라 진행된다는 것을 알 수 있었다.

MDABM and MDAEW, as a accelerating weight loss agents, were prepared by adding water to myristyldimethylbenzylammonium bromide(MDAB) and myristyldimethylethylammonium ethyl sulfate (MDAE) synthesized. As a result of weight loss finishing of the MDABW and MDAEW with NaOH on PET fiber, the ratio of weight loss of MDABW was very larger than that of MDAEW. This result showed that quaternary ammonium bromide had higher weight loss effect than quaternary ammonium sulfate, and the ratio of weight loss was greatly varied with the kind of quaternary ammonium salts used. In these conditions, proper treatment concentration, treatment time, and treatment bath ratio were about 8g/l, 6O~90min, and 40:1~50:1, respectively.

For the purpose of producing emulsified fire proofing agent for synthetic fibers, 2,3-dibromopropylmonoamido orthophosphate[DP-AOP] and bis(2,3-dibromopropyl)monoamidoorthophosphate[(DP)2AOP] were synthesized, and their structures were identified by instrumental analysis, respectively. Using three kinds of emulsifiers, O/W emulsified fire proofing agents, DPF and DPDPF, were obtained corresponding to DP-AOP and (DP)2-AOP, respectively. Various synthetic textiles were fire-retardant treated by prepared DPF and DPDPF, and fire retardancy and tearing strength of the resulting products were tested. The results showed that as the concentration of fire proofing agents increased, fire retardancy increased, but the tearing strength much decreased, where the tendencies of DPDPF were deeper than those of DPF. But, since the fire retardancy appeared favorable in the range of 10~20wt% of DPDPF, DPDPF is proven to be a fire proofing agent useful for various synthetic textiles.

n-Octyldimethylbenzylammonium chloride, dodecyldimethylbenzylammonium chloride, and octadecyldimethylbenzylammonium chloride were synthesized to be used as the accelerating weight loss agent. These synthesized compounds were used for the weight loss treatment of PET textile with sodium hydroxide. From the treatments, it was found that the lower carbon number of high alkyl group existed in quaternary ammonium salts, the better effect of weight loss was acquired. The proper concentration of accelerating weight loss agent was 8~10g/l, the proper treatment time was 60~90 minutes, the proper treating bath ratio was 1 : 50. It is proved that n-octyldimethylbenzylammonium chloride and dodecyldimethylbenzylammonium chloride are good accelerating weight loss agent.

In order to analysis creep characteristics and elastic recovery of the high-tech fibers for fishing gear materials, creep and elasticity tests were carried out on netting twines made of nylon, kevlar 29 and techmilon respectively. After creep tests, the rupture surface of raw materials was observed by scanning electron microscope(SEM). The results obtained are as follows: 1. Netting twines were arranged in order of creep rupture time as follow: techmilon, kevlar 29, nylon. The creep progressive pace was the fastest in techmilon. 2. In order of the creep elongating, netting twines were arranged as follows: nylon, techmilon, kevlar 29. 3. The rupture time T sub(r) decreased almost linearly with the increase of applied load L on the log-log scaled graph. The empirical equations computed for kevlar 29 and techmilon are as follows: T sub(r kevlar 29)=1.9512×1037L super(-15.773). T sub(r techmilon)=2.7146×1016L super(-6.831). 4. It was observed by SEM that creep was progressed in all netting twines. The difference of rupture morphology was recognized clearly in tensile and creep tests. 5. In order of the elastic recovery, netting twines were arranged as follows: techmilon, kevlar 29, nylon.

In order to analysis the tensile properties of the high-tech fibers for fishing gear materials. tensile strength was tested on raw materials, single yarns and netting twines(plied yarns)made of nylon, kevlar 29 and techmilon respectively. The results obtained are as follows: 1. The tensile stress and tenacity of unknotted single yarns in dry and wet conditions were 3 to 3.5 times greater in the high-tech fibers than in nylon. But the elongation of the high-tech fibers was about 15% of that in nylon. 2. The tensile strength of knotted single yarns in dry and wet conditions was arranged in order of as follows : techmilon. kelver 29, and nylon. The ratio of knot strength to tensile strength, knot efficiency, was the highest in nylon. 3. The tensile strength of unknotted netting twines in dry and wet conditions was 2.3 to 2.5 times greater in the high-tech fibers than in nylon. 4. The tensile strength of knotted netting twines in dry and wet conditions was arranged in order of as follows : techmilon, kevlar 29, nylon. The knot efficiency was the highest in nylon.

섬유보강 시멘트계 복합재료 (이하 FRCC)는 균열 폭의 제어 등의 역학적인 효과뿐 아니라 철근방식에도 효과가 있는 것이 기존의 문헌으로부터 확인되고 있다. 본 연구에서는 아연섬유를 포함한 각종 금속섬유를 이용하여 철근의 방식효과를 부식 촉진 실험에 의해 검토했다. 더욱이 방식효과에 큰 영향을 미치는 염분침투, 희생양극 효과, 전기회로 형성에 주목하여, 각각의 요인에 있어서 검토를 실시했다. 그 결과, 금속섬유를 혼입한 FRCC의 방식효과를 확인할 수 있었으며, 특히 희생 양극효과가 높은 아연섬유의 경우, 염분침투 억제 효과가 뛰어나 내부식 성능이 향상되는 것을 확인할 수 있었다.

This paper describes the mechanical properties of high strength concrete with 1,600 MPa strength steel fiber. The fiber aspect ratio and fiber volume fraction used in this study is 80 and 0.75%. The Cylindrical specimens with ∅150×300 mm and the prisms with 150×150×550 mm were mad and tested in accordance with KS F2403 and ASTM C1609. As the result, specimens with high strength fiber has superior performance then that with normal strength fiber.

This research provides a method that can be conveniently and easily to apply the prestressing force to concrete structures incorporating shape memory alloy fibers. For this, discrete shape memory alloy fibers were manufactured to be mixed with cement mortar. Then shape memory effect was generated to evaluate uplift displacements at the mid-span of the mortar beams with increasing fiber volume fractions.

This paper is focused on flexural bahavior of cement composites reinforced with carbon fibers as a part of research for improving a seismic performance of structures using carbon fiber reinforced concrete(CRFC). Flexural behavior test was conducted on respective specimens reinforced with different fiber length(6mm, 12mm) and contents(0%, 0.5%, 1.0%, 2.0%, 3.0%). The result of the test showed that the flexural performance of carbon fiber reinforced cement composites are directly proportional to the fiber contents except for the specimen reinforced with 3% carbon fiber.

일반적인 고인성․고성능 시멘트 복합재료의 경우 균질한 재료분포를 위하여 기본적으로 굵은 골재를 배재하는 경향이 있다. 그러나, 굵은 골재를 배재한 섬유 복합 시멘트 모르타르의 경우 재료의 탄성계수가 낮으며 단위시멘트량이 높아 경제성과 효율이 낮은 배합이기 때문에 대량으로 신규 구조물에 적용하기 힘들다. 따라서, 본 연구에서는 적절한 수준의 굵은 골재를 혼입하였지만 여전히 휨인성과 휨강도는 확보하고 있는 동시에, 균열 분산성능도 보유하고 있는 고인성 섬유보강 콘크리트에 대한 개발 연구를 수행하였다. 굵은 골재의 혼입량을 실험 변수로 실험 연구를 수행하였고, 결과에 따르면 고인성 모르타르의 기본 배합에 굵은골재를 잔골재의 25%중량비로 추가한 경우에서 가장 좋은 휨인성 그리고 균열분산 특성을 나타내었다. PVA섬유는 균열분산과 연성 증진에 효과적이었고, 강섬유 섬유의 경우 균열분산보다는 강도 증진에 효과적이었다.

Background : Bamboo fiber contains 97% of dietary insoluble fiber from mature bamboo shoots. Bamboo contains phytosterols and a high amount of fiber which can be labelled as nutraceuticals or natural medicines that are attracting attention from the aspect of health. This study was conducted for the production of dietary fiber from Sinoarundinaria nigra, S (S. nigra) shoots barks by using α-amylase, alcalase, glucoamylase or Viscozyme and improvement of Large intestinal function in rats. Methods and Results : Yields of enzymatic degradation were 80.5% (322 g/400g) and the dietary fiver content of the enzyme digest was 69.7%. Sprague-Dawley rats were fed on diet containing 100 ㎎/㎏ and 200 ㎎/㎏ S. nigra dietary fibers [dietary fiver of bamboo shoots barks (SNDFB)] for one weeks. As a result of weighing of the fecal pellets, loperamide alone group showed a significant decrease compared with the control group, and it was significantly increased in test group (200 ㎎/㎏-SNDFB) compared to loperamide alone group. In addition, the measurement of gastrointestinal charcoal transit ratio in rats, loperamide alone group showed a significant decrease compared with the control group, and it was significantly increased in all the test substance groups compared to loperamide alone group. The number of remnant fecal pellets in the colon after dissection was significantly increased in the loperamide alone group compared to the control group, and was significantly decreased in the test substance groups compared to loperamide alone group. Conclusion : These results suggest that dietary fiber isolated from S. nigra has a marked effect on the improvement of bowel function in rats with loperamide (4 ㎎/㎏)-induced constipation.

This study investigates the effects of compressive strengths on mechanical properties of concrete with compressive strengths of 40 and 80 MPa. In this study, The steel fiber an aspect ratio of 64 and a tensile strength of 1,600 MPa used. As the result, There are no significant effect of fiber tensile strength on mechanical properties of normal strength SFRC. For high strength SFRC, Specimen with high strength fiber have superior performance then that with normal strength fiber.

게르마늄은 세계적으로 고가의 희소금속 중 하나로 국내에서는 게르마늄 광산이 없으며, 전량 수입에 의존하고 있는 금속이다. 게르마늄 주요 용도는 PET 수지 제조용 촉매, 광섬유, 반도체 등 국가 주력산업의 핵심 소재로 광범위하게 사용된다. 특히, 광섬유에는 1km당 0.54g의 게르마늄을 함유하고 있으며, 관련기술 미비로 국내외 모두 재활용이 시도되지 않고 있으므로, 기술 선점 시 그 파급효과가 매우 클 것으로 판단되어진다. 따라서 본 연구는 폐 광섬유에서 게르마늄을 경제적으로 회수할 수 있는 가능성을 입증하기 위해 pyrometallurgy와 hydrometallurgical reactions을 결합한 하이브리드 방식을 통해 게르마늄 농축을 하고자 하였으며, 반응 온도, 반응 시간 등을 변화 시키며 게르마늄 농축 거동을 관찰하였다.

A notch beam test has been carried out for SFRC-SCC for precast slab tracks in accordance with BS-EN-14651. The steel fiber used is a product of Beckert, which is further processed with a general steel fiber and a steel fiber end(named as 3D, 5D). Overall, the crack behavior of the specimen using 5D fiber was superior to that of using 3D fiber

This study evaluated the orientation control of steel fibers in cementitious materials using magnetic field. With the increases in the range of the magnetic field, the effective length of the orientation control of the steel fiber is increased and the orientation control effect is larger.

This study evaluated the influence of nozzle shapes in the orientation of fibers in cementitious materials. The nozzle shapes involved in the study are conventional, balded, and tapered circulars. The results showed that both the bladed and tapered nozzles increased the control performance of fiber orientation compared to the conventional nozzle. In particular, bladed nozzle was more effective in controlling the fiber orientation.

In this study, five high intelligent concrete (HIC) test specimens were fabricated by reinforcing the cement mortar with garnet, fiber (nylon and polypropylene), and shape memory alloy (SMA), to examine the effects of the numbers and positions of the reinforcements on the physical characteristic of the SMA. In improving the yield strength and structural self-rehabilitation capability, two or more hybrid fiber, PP and SMA reinforcements, as in SMA-PP, SMA-NP, SMA-2 yielded better results than SMA-1.

The purpose of study is to investigate properties of high strength concrete in fire. Composite fibers that are mixed in concrete are used to improve vulnerable point. The role of each fiber is to prevent of spalling effect and improve of flexural strength.