PURPOSES : This paper presents the experimental results of tests conducted on concrete produced with air-cooled (AS) and water-cooled (WS) ground blast-furnace slag exposed to multi-deterioration environments of carbonation and scaling. METHODS : Carbonated and uncarbonated concrete specimens were regularly monitored according to the ASTM C 672 standard to evaluate the durability of concrete exposed to both scaling and combined carbonation and scaling conditions. Additionally, mechanical properties, such as compressive strength, flexural strength, and surface electric resistivity, were analyzed. RESULTS : It was found that concrete specimens produced with AS and WS had a beneficial effect on the mechanical properties because of the latent hydraulic properties of the AS and WS mineral admixtures. Moreover, carbonated concrete showed good scaling resistance in comparison to uncarbonated concrete, particularly for concrete produced with AS and WS. CONCLUSIONS : The improved scaling resistance of carbonated concrete showed that AS is a suitable option for binders used in cement concrete pavements subjected to combined carbonation and scaling.

본 연구에서는 고로슬래그 미분말 및 플라이애시와 같은 광물질 혼화재를 사용한 친환경 고성능 3성분계 시멘트 콘크리트 교면 포장의 성능을 평가하기 위하여 실험을 하였다. 광물질 혼화재의 혼입률 변화에 따른 3성분계 시멘트 콘크리트의 최적배합을 찾기 위하여 압축강도 및 휨강도 시험을 하였으며 최적배합을 사용하여 내구성 시험인 염소이온 침투저항성, 동결융해, 박리 저항성, 균열 저항성 및 알칼리골재반응 시험으로 친환경 고성능 3성분계 시멘트 콘크리트 교면 표장의 내구성 평가 및 신 구 콘크리트의 부착력을 평가하기 위하여 부착강도 시험을 하였다. 시험결과, 시멘트 70%, 고로슬래그 미분말15% 및 플라이애시 15%의 배합 바인더에서 압축강도 및 휨강도가 우수하게 나타났으며 이를 최적배합으로 도출하였다. 실내 및 시험시공에서 최적 배합을 사용한 실험결과는 염소이온 침투 저항성, 동결융해 저항성, 표면박리 저항성, 알칼리골재 반응 억제 및 내마모성이 우수하게 나타났다. 또한, 특수 제작된 Polymer Cement Mortar(Brooming)를 사용한 신 구 콘크리트의 부착력에서도 우수한 성능을 나타냈다.

본 연구는 고성능 폴리머 시멘트계 프리캐스트 제품의 개발 및 미세균열 발생 시 자기치유기능을 확보할 목적으로 경화제 무첨가 EMM의 물리적 성질을 검토하고, 그 물성에 영향을 끼치는 시멘트 매트릭스 내의 에폭시수지 경화도와 현미경을 통한 조직구조의 관찰과 함께 자기치유효과를 검토하였다. 그 결과, 경화제 무첨가 EMM의 폴리머 혼입에 의한 강도 개선 효과는 인장강도, 휨강도, 압축강도의 순으로 나타났다. 접착성은 콘크리트 피착체의 모세관 공극에 폴리머 필름의 형성에 기인한 투묘효과에 기인하여 크게 향상되었다. 투수저항성은 폴리머 결합재비 20% 및 고로슬래그 미분말 치환율 30%를 병용한 EMM에서 보통시멘트 모르타르 대비 97%의 감소율을 나타내 매우 우수하였 다. 고로슬래그미분말, 팽창재 및 황산나트륨을 병용한 EMM의 균열 폭은 고로슬래그 치환율이 증가함에 따라 미미하게 감소하였으나, 고로 슬래그미분말 치환율 20%에서 수중침지기간의 증가와 함께 서서히 균열부 자기폐색 효과를 관찰할 수 있었다.

양생조건에 따른 고로슬래그를 혼입한 콘크리트의 염화물 이온 확산계수의 변화를 관찰하기 위하여 GGBFS 혼입율 0%, 30%, 60%로 구분하고 W/B를 40%,50%,60%로, 양생조건을 기중양생과 수중양생으로 시험체를 제작하여 콘크리트 염화물 이온 확산계수 평가를 실시하였다. 평가결과 GGBFS의 치환율이 증가할수록 콘크리트 염화물이온 확산계수는 감소하였지만, 양생조건에 따른 확산계수 편차가 증가하는 것을 확인하였다. 특히 W/B가 증가할수록 그 차이는 증가하였으며. W/B 60% 조건에서 수중양생 대비 기중양생 시험체의 염화물 이온 확산계수는 2배 가까이 증가하는 것을 확인하였다.

고분말도 슬래그를 사용할 경우 초기재령에서의 강도발현은 우수하나 수화열 및 품질관리에 따른 문제가 발생하기 쉽다. 본 연구 에서는 3000급 저분말도의 고로슬래그 미분말을 혼입한 콘크리트의 강도특성 및 내구특성을 분석하였다. 작업성을 기준으로 3가지 배합을 고려하였으며, 압축강도와 내구특성시험이 수행되었다. 강도특성 결과 3000급 슬래그를 혼입한 콘크리트는 28일 재령에서 OPC(Ordinary Portland Cement) 배합 대비 강도가 떨어지지만 장기재령에서는 잠재수경성의 촉진으로 인하여 큰 차이가 나타나지 않았다. 탄산화 및 동결융해 실험에서는 4200급 슬래그 배합 대비 약간 우수한 저항성능이 나타났는데, 이는 동일 슬럼프를 목표로 배합을 진행하여 3000급 슬래그 배합에 단위수량을 적게 고려하였기 때문이다. 장기재령의 경우, 3000급 슬래그 배합의 염화물확산계수는 OPC 배합 대비20% 수준으로 감소하여 우수한 내염해특성이 평가되었다. 단위수량을 조정하고 3000급 저분말도의 고로슬래그 미분말을 혼입하여 사용할 경우, 기존 분말도의 슬래그가 사용된 콘크리트 및 OPC 콘크리트와 비교시 우수한 작업성능과 내구특성을 확보할 수 있을 것으로 판단된다.

대표적인 콘크리트 혼화재료 중 하나인 고로슬래그 미분말을 혼입한 콘크리트는 잠재수경성에 의해 콘크리트의 장기 내구성능 및 역학적 성능이 향상된다. 본 연구에서는 3 가지 수준의 물-결합재 비(0.37, 0.42, 0.47) 및 고로슬래그 미분말 혼입률(0 %, 30 %, 50 %)을 고려하여 염해에 대한 내구성능 평가를 수행하였으며, 염화물 확산 거동(촉진 염화물 확산계수, 통과 전하량)을 예측하는 식을 도출하고 촉진 염화물 확산계수와 통과 전하량간의 상관관계를 평가하였다. 2년 양생조건 시 고로슬래그 미분말 혼입 콘크리트에서 OPC 콘크리트 대비 촉진 염화물 확산계수 평가 결과에서는 최대 28 %의 감소율을 통과 전하량 평가에서는 최대 29 %의 감소율을 나타냈다. 또한 물-결합재 비의 증감에 의한 영향을 OPC 콘크리트 보다 GGBFS 미분말 혼입 콘크리트에서 더 적게 받는 것으로 판단된다. 배합 특성 및 실험 결과를 바탕으로 촉진 염화물 확산계수 및 통과 전하량을 예측하는 식을 다중회귀분석을 통해 도출한 결과, 통과 전하량 예측식이 확산계수 예측식보다 높은 결정계수를 나타냈다.

In this paper, the changing of durability design variables such as cover depth, surface chloride content, and replacement ratio of GGBFS are considered, and optimum substitution ratio of GGBFS are derived with intended service life. With increasing cover depth, service life increased by 2.78~3.21 times. Cover depth is the most influencing parameters of those in this study. For reasonable durability design of concrete, quantitative exterior condition and critical chloride content should be determined.

최근 온실가스 감축을 위해 시멘트 클링커를 대체하여 고로슬래그 미분말을 다량 치환한 하이볼륨 슬래그 시멘트에 대한 연구 활 발히 진행되고 있다. 하지만, 수화열 및 내구성 등 다양한 장점에도 불구하고 초기 재령에서의 낮은 강도 발현 등의 문제점으로 인해 실제 현장 의 적용에 한계점을 가지고 있다. 본 연구는 이러한 점을 극복하고자 GGBFS 혼입률에 따른 페이스트의 압축강도, 수화열 등의 특성을 분석하 였다. GGBS 분말도에 따른 4종류와 치환율 35%, 50%, 65%, 80% 4수준으로 하여 총 16개의 배합에 대해 실험을 수행하였다. 실험결과 낮은 물-바인더 비에 의한 고성능 하이볼륨 슬래그 시멘트 페이스트 배합은 초기 재령에서의 낮은 압축강도의 한계점을 극복할 수 있을 것으로 판단된 다. 또한 GGBS의 분말도는 고성능 하이볼륨 슬래그 시멘트 페이스트의 초기 재령에서의 압축강도 증진에는 효과가 있지만, 28일 이후의 장기 강도에는 큰 영향이 없는 것으로 나타났다.

고로슬래그 미분말은 공학적으로 우수한 건설산업 부산물이며, 최근들어 환경부하 저감 및 사용 활성화를 위해 대단위 슬래그 치 환 콘크리트가 많이 연구되고 있다. 본 연구에서는 목표 강도를 50 MPa로 설정하고 고로슬래그미분말 치환률을 65%로 고려한 대단위 치환 슬 래그 콘크리트를 제조하여 건조수축특성과 초지재령 특성을 평가하였다. 이를 위해 3 수준의 콘크리트를 제조하였으며, 슬럼프 플로우, 강도, 건조 및 자기수축에 대한 실험을 수행하였다. 실험결과, 보통 포틀랜트 시멘트를 100% 함유한 콘크리트(OPC 100)에 비하여 재령 7일전의 강 도는 약간 감소하였으나, 슬래그 치환 배합은 수화에 필요한 충분한 자유수를 가졌으므로 28일 재령에서는 우수한 강도 발현을 나타내었다. 또 한 재령 3일까지 큰 자기수축으로 인하여, OPC 100 배합에서는 건조수축이 크게 평가되었지만, 65% 고로슬래그 미분말을 치환한 배합에서는 초기재령의 자기수축 성능이 개선되어 우수한 건조수축거동을 나타내었다. 특히 단순 질량 치환배합(BS 65)보다 물-결합재비(0.27)와 단위수 량(163kg/m3)을 낮춘 OPTBS 65에서 더욱 우수한 건조수축 및 자기수축 거동을 나타내었다.

In this study, it was developed geopolymer concrete of alkali-activated using the mixed fly ash and blast furnace slag. and it was developed the interlocking block using the developed geopolymer concrete. In addition, the bending strength and water absorption rate of the interlocking block was tested by KS standard. The test results were as follows. The water adsorption ratio of the BSF4 specimen was under 10%, and the flexural strength of that was over 5MPa

In this study, it was developed geopolymer concrete of alkali-activated using the mixed fly ash and blast furnace slag. and it was developed the interlocking block using the developed geopolymer concrete. In addition, the bending strength and water absorption rate of the interlocking block was tested by KS standard. The test results were as follows. The water adsorption ratio of the BSF4 specimen was under 10%, and the flexural strength of that was over 5MPa.

철근 콘크리트 구조물의 철근에 대한 부식을 발생시키는 다양한 유해 열화인자 중 염화물 이온(Cl-)은 침투로 인한 확산속도가 빠 르고, 철근에 직접적으로 관여하여 부식을 야기시켜 매우 중요한 열화원인이다. 대형 콘크리트 구조물의 타설에서 불가피하게 발생하는 콜드 조인트는 전단력에 취약하여, 이는 내구적 열화에 대한 피해를 증가시키는 경향을 보인다. 본 연구에서는 콜드조인트를 가진 OPC(Ordinary Portland Cement) 콘크리트와 GGBFS(Ground Granulated Blast Furnace Slag) 염화물 촉진 실험으로 염화물 확산계수를 정량적으로 평가하였 다. GGBFS 콘크리트에서는 6.6×10-12 m2/sec의 확산계수가 측정되었는데. 이는 OPC 콘크리트에 비하여 약 30% 수준의 낮은 확산계수값을 나 타내었으며, 콜드조인트를 가진 콘크리트에서도 비슷한 경향이 관측되었다. OPC 건전부 콘크리트에 비하여 GGBFS 콘크리트의 염화물 확산 계수는 건전부에서 0.30배, 콜드조인트부에서 0.39배 정도의 우수한 염해 저항성을 나타내었다.

Using of the ground granulated blast furnace slag as the substitutes of cement mixtures is increasing. This is used about 40% as the substitutes commercially but recently there are several tests used the maximum 80%. When used as the substitutes of cement mixtures which can improve the durability, the watertightness and the sulfate resistance but there is reduced the concrete quality due to early strength reduction and the drying shrinkage increase. Therefore it is very important to make the curing environment which helps early hydration activation vigorously. In this study, the hydrate characteristics replacing the maximum 80% of ordinary portland cement with blast furnace slag powder and using the alkali activator to increase early hydration activation were considered and analyzed by the XRD, TG-DTA, SEM, From these tests results, the use of the alkali activator had the increase of the calcium hydroxide according to ages and the reach time reduced about 1 min. and 9 min. for the first and second peak respectively. The effects on the hydrate characteristics of using the alkali activator were not significant.

The study is compressive strength of 110MPa PHC pile using ground granulated blast furnace slag to NAC, AC curing method. In the result, 20% of ground granulated blast furnace slag could be substituted for cement in PHC pile concrete.

In experimental results, the prediction equation for 28 day-strength of GGBF slag concrete could be produced through the linear regression analysis of early strength and 28 day-strength. In order to acquire the reliability, all mixture were repeated as 3 times and each mixture order was carried out by random sampling. The prediction equation for 28 day-strength of GGBF slag concrete by 1 day strength won the good reliability.

본 연구는 혼합 활성화제에 의한 알칼리 활성화 슬래그 시멘트(AASC)의 역학적 특성에 관한 연구이다. 사용된 활성화제는 황산칼슘(CaSO4, 이하 CS), 황산나트륨(Na2SO4, 이하 SS) 및 수산화나트륨(NaOH)이다. 황산염은 슬래그 중량의 2.5, 5.0, 7.5 및 10.0%로 치환하여 사용하였으며, NaOH는 2M 및 4M 농도의 수용액으로 사용하였다. 본 연구에서는 황산염(CS 및 SS) 치환율에 따른 배합(4가지 배합)과 2M 및 4M의 각각의 NaOH 수용액에 치환된 황산염을 혼합하여 시험체를 제작하였다. 시험체는 총 24가지의 배합에 따라 페이스트로 제작되었으며, 물－결합재 비는 0.5로 하였다. 경화된 시험체에 대해서 압축강도, 휨강도, 초음파속도(UPV), 흡수율 및 XRD 분석을 수행하였다. CS의 활성화제를 사용한 경우는 7.5% CS 치환율, 2M NaOH 수용액+ 5.0% CS 치환율 및 4M NaOH 수용액+ 5.0% CS 치환율의 시험체에서 최고의 압축강도를 나타내었다. 또한, SS의 활성화제를 사용한 경우는 10.0% SS 치환율, 2M NaOH + 7.5% SS 치환율 및 4M NaOH + 2.5% SS 치환율에서 최고의 압축강도 발현을 나타내었다. 휨강도, UPV 및 흡수율은 압축강도 발현 결과와 유사한 경향을 나타내는 것을 알 수 있었으며, XRD 분석결과 시험체 내에 생성된 반응물질은 ettringite, CSH 및 실리케이트계 수화물인 것으로 나타났다. AASC에서 황산염과 NaOH의 혼합 사용은 황산염의 단독 사용의 경우와 비교하여 일정 수준의 농도 범위에서 강도를 향상시키고 조직을 치밀화 시키는 등의 긍정적인 영향을 미치는 것으로 판단된다.

In experimental results, the prediction equation for 28 day-strength of GGBF slag concrete could be produced through the linear regression analysis of early strength and 28 day-strength. In order to acquire the reliability, all mixture were repeated as 3 times and each mixture order was carried out by random sampling. The prediction equation for 28 day-strength of GGBF slag concrete by 1-day strength won the good reliability.

Concrete with blast furnace slag (BFS) shows varied strength development properties different from normal concrete. Therefore, a precise prediction of compressive strength using a full maturity model is desired. The purpose of this study is to predict the compressive strength of concrete with BFS by calculating the apparent activation energy (Ea) and rate constant (kT) for each BFS replacement ratio. The method of Carino Model is used in this study for predicting compressive strength of concrete with BFS.